Preparation and evaluation of Au nanoparticle–silica aerogel nanocomposite

Preparation and Characterization of Silica Aerogel Microspheres

Silica aerogel microspheres based on alkali silica sol were synthesized using the emulsion method. The experimental results revealed that the silica aerogel microspheres (4-20 µm in diameter) were mesoporous solids with an average pore diameter ranging from 6 to 35 nm. The tapping densities and specific surface areas of the aerogel microspheres are in the range of 0.112-0.287 g/cm³ and 207.5-66...

exploring motivation and english test preparation strategies of iranian pre-university candidates during and at the end of test preparation period for konkur examination

the current study aimed at investigating the relationship between motivation and test preparation strategies (tpss) used by iranian pre-university students in their preparation period for the university entrance exam (uee). due to the importance of uee in iran, this study also attempted to show its impact on these two important variables. to this end, 100 pre-university students in an iranian p...

Preparation of Pectin–ZnO Nanocomposite

Pectin-ZnO nanocomposite was prepared in the aqueous solution condition at room temperature. The Fourier transform infrared, X-ray diffraction, and transmission electron microscope (TEM) measurements confirmed the nanoscaled structure of pectin-ZnO composite. According to the TEM observation, the average composite granules size was about 150 nm and the embedded ZnO nanoparticles were uniform wi...

Chemical Synthesis of PEDOT–Au Nanocomposite

In this work, gold-incorporated polyethylenedioxythiophene nanocomposite material has been synthesized chemically, employing reverse emulsion polymerization method. Infrared and Raman spectroscopic studies revealed that the polymerization of ethylenedioxythiophene leads to the formation of polymer polyethylenedioxythiophene incorporating gold nanoparticles. Scanning electron microscope studies ...

Preparation and characterization of Ni-doped carbon aerogel for supercapacitor