Preparation and Characterization of Organic-Inorganic Hybrid Hydrogel Electrolyte Using Alkaline Solution
نویسندگان
چکیده
منابع مشابه
Preparation and Characterization of Organic-Inorganic Hybrid Hydrogel Electrolyte Using Alkaline Solution
Organic-inorganic hybrid hydrogel electrolytes were prepared by mixing hydrotalcite, cross-linked potassium poly(acrylate) and 6 M KOH solution. The organicinorganic hybrid hydrogel electrolytes had high ionic conductivity (0.456–0.540 S cm) at 30 °C. Moreover, the mechanical strength of the hydrogel electrolytes was high enough to form a 2–3 mm thick freestanding membrane because of the reinfo...
متن کاملpreparation and characterization of new co-fe and fe-mn nano catalysts using resol phenolic resin and response surface methodology study for fischer-tropsch synthesis
کاتالیزورهای co-fe-resol/sio2و fe-mn-resol/sio2 با استفاده از روش ساده و ارزان قیمت همرسوبی تهیه شدند. از رزین پلیمری resol در فرآیند تهیه کاتالیزور استفاده شد.
Preparation and Characterization of a Cotton-Based Nanocomposite Hydrogel
In this work, hydrogel nanocomposites were synthesized by solution polymerization of acrylic acid (AA) and itaconic acid (IA) in the presence of cotton fabric. Ammonium persulfate (APS) was used as the polymerization initiator in the presence of a crosslinker, methylene bisacrylamide (MBA). Insertion of Ag followed by reduction of Ag+ cations results in a hydrogel nanocomposite. The ...
متن کاملSynthesis and characterization of inorganic-organic hybrid gallium selenides.
Two semiconducting hybrid gallium selenides, [Ga6Se9(C6H14N2)4][H2O] (1) and [C6H14N2][Ga4Se6(C6H14N2)2] (2), were prepared using a solvothermal method in the presence of 1,2-diaminocyclohexane (1,2-DACH). Both materials consist of neutral inorganic layers, in which 1,2-DACH is covalently bonded to gallium. In 1, the organic amine acts as a monodentate and a bidentate ligand, while in 2, bident...
متن کاملControllable lasing performance in solution-processed organic-inorganic hybrid perovskites.
Solution-processed organic-inorganic perovskites are fascinating due to their remarkable photo-conversion efficiency and great potential in the cost-effective, versatile and large-scale manufacturing of optoelectronic devices. In this paper, we demonstrate that the perovskite nanocrystal sizes can be simply controlled by manipulating the precursor solution concentrations in a two-step sequentia...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Polymers
سال: 2011
ISSN: 2073-4360
DOI: 10.3390/polym3041600