Precisely-Controlled Synthesis of Oxide Powders by Polymerizable Complex Method Towards High-Performance
نویسندگان
چکیده
منابع مشابه
Synthesis of high-purity YbBa2Cu3O7−d and LuBa2Cu3O7−d superconductors by polymerizable complex method
Polycrystalline samples of YbBa2Cu3O71d and LuBa2Cu3O71d were prepared by polymerizable complex method. The combined results of both X-ray diffraction and Raman scattering analyses indicated that YbBa2Cu3O71d sample was of single phase when the samples were sintered in a low oxygen partial pressure (1%) at relatively low temperature (845°C). On the other hand, LuBa2Cu3O71d sample was only sligh...
متن کاملSYNTHESIS OF AL2O3-NI COMPOSITE POWDERS BY CO-PRECIPITATION METHOD
The synthesis of micro-sized, uniformly distributed Al2O3-15Vol% Ni powders were studied through three step co-precipitation of hydroxides mixtures from proper solution, calcination at air atmosphere and final step of calcined powders in a carbon bed. Al and Ni hydroxide and amorphous phase were first obtained from their salt’s solutions through chemical co-precipitation method by adjusti...
متن کاملSynthesis of Carbon Spheres of Controlled Size by Hydrothermal Method
Carbon Spheres were fabricated by hydrothermal method and their structural properties were investigated. Carbon Spheres with average sizes around of 230, 320 and 430 nm were synthesized in different concentration of glucose aqueous solution and different hydrothermal reaction time. The temperature of 180 °C by a hydrothermal reaction was fixed in all of glucose concentration and hydrothermal re...
متن کاملSynthesis of HfB2 Powders by Carbothermal Reduction
In this research, solid state carbothermal synthesis of HfB2 Nano powders was investigated. For this purpose, HfO2,H3BO3, carbon active or phenolic resin were used as raw materials for carbothermal reaction. After 2-4 hours of milling the raw materials by a planetary ball in an ethanol media, the mixture was heat dried and pressed in to disks under pressure of 20-30 bar. The disks were then pla...
متن کاملSynthesis of Chromium Oxide Nano Particles by Thermal Decomposition Method
Disclosed is a method of preparing pigmentary chromium oxide nano particles having 50 percent particle size less than about 100 nm. Preparation of nano chromium (III) oxide is investigated by thermal decomposition method. According to the disclosed method, a substantially dry solid composition of potassium dichromate and carbon active is heated in CO2 atmosphere to a temperature of about 60...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 2007
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.54.32