Precipitation reaction in alpha-Cu-Al-Ag alloys
نویسندگان
چکیده
منابع مشابه
Clustering and Segregation of Mg and Ag Atoms during the Precipitation Processes in Al(-Li)-Cu-Mg-Ag Alloys
This paper reports three dimensional atom probe (3DAP) results of solute clusters and precipitates in early aging stages of Al-Cu(-Li) alloys containing small amounts of Ag and Mg atoms. In an as-quenched Al-1.9Cu-0.3Mg-0.2Ag (at.%) alloy, solute atoms are uniformly dissolved. On aging for 5 s at 180°C, Ag and Mg atoms form co-clusters. These co-clusters do not have well defined shape, but they...
متن کاملINFLUENCE OF THE Al CONTENT ON THE PHASE TRANSFORMATIONS IN Cu-Al-Ag ALLOYS
The literature about alloys of the Cu-Al system is extensive, due to its practical use. These alloys are of low cost and present good strength and hardness, depending on the Al content. They are used for making sleeves, guides, seats, flanges, gear wheels and many other critical small parts, as electrolysis cell cathodes, circuit plates and casting moulds when high thermal conductivity is neede...
متن کاملRoom temperature precipitation in quenched Al - Cu - Mg alloys : a model for the reaction kinetics and yield strength development
The microstructural evolution during low temperature ageing of two commercial purity alloys (Al1.2Cu-1.2Mg-0.2Mn and Al-1.9Cu-1.6Mg-0.2Mn at.%) was investigated. The initial stage of hardening in these alloys is very rapid, with the alloys nearly doubling in hardness during 20 h ageing at room temperature. The microstructural evolution during this stage of hardening was investigated using diffe...
متن کاملPrecipitation hardening in dilute Al–Zr alloys
The aim of this study was to investigate the effect of solute content (hipoperitectic Al–0.22 wt.%Zr and hiperperitectic Al–0.32 wt.%Zr) on the precipitation hardening and microstructural evolution of dilute Al–Zr alloys isothermally aged. The materials were conventionally cast in a muffle furnace, solidified in a water-cooled Cu mold and subsequently heat-treated at the temperature of 650 K (3...
متن کاملElemental separation in nanocrystalline Cu-Al alloys
Y. B. Wang, X. Z. Liao, Y. H. Zhao, J. C. Cooley, Z. Horita, and Y. T. Zhu School of Aerospace, Mechanical and Mechatronic Engineering, The University of Sydney, Sydney, NSW 2006, Australia School of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094, China Division of Materials Science and Technology, Los Alamos National Laboratory, Los Alamos, New ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Matéria (Rio de Janeiro)
سال: 2011
ISSN: 1517-7076
DOI: 10.1590/s1517-70762011000300002