Preannealing effect and soft magnetic properties of the nanocrystalline Fe74CulNb3Si12B10 alloy
نویسندگان
چکیده
منابع مشابه
Magnetic and Electrical Properties of Nanocrystalline Fe85Si10Ni5/Phenolic Resin Soft Magnetic Composites
In this work, nanocrystalline Fe85Si10Ni5 soft magnetic powders were prepared by mechanical alloying and subsequent annealing to reduce the internal stresses and lattice strains. The powders were mixed with phenolic resin and warm pressed to produce nanostructured soft magnetic composites. The effect of annealing time and temperature on the crystalline structure, microstructure and magnetic pro...
متن کاملSoft magnetic properties of nanocrystalline Fe73B7Si16Nb3Cu1 alloy after rapid heating under tensile stress
Amorphous Fe73B7Si16Nb3Cu1 ribbon was crystallized rapidly by electric current heating under simultaneously applied tensile stress along the ribbon axis. As a result, strong transverse magnetic anisotropy was induced in the ribbon. Dynamic magnetic properties of the ribbons rapidly heated either under the tensile stress or without tensile stress were measured using toroidal cores. Optimal elect...
متن کاملNanocrystalline Soft Magnetic Alloys
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 417
متن کاملProduction of Nanocrystalline (Fe, Co)-Si-B-P-Cu Alloy with Excellent Soft Magnetic Properties for Commercial Applications
With the aim of applying to a magnetic core material, the effect of ribbon thickness on the magnetic properties of a (Fe, Co)-Si-B-P-Cu alloy ribbon was investigated. It is found that the Si addition in (Fe, Co)-Si-B-P-Cu nanocrystalline alloy increased the saturation magnetic flux density (Bs), but degraded the coercivity (Hc), suggesting that the Si addition should be suppressed to a little a...
متن کاملAmorphous and Nanocrystalline Soft Magnetic Materials
Annealing of amorphous precursor alloys, with compositions (Fe,Co!88M7B4Cu1 ~M5Zr, Nb, Hf!, above their primary crystallization temperature results in the nanocrystallization of the ferromagnetic a8-FeCo phase. This work describes results of the characterization of these alloys, including morphological and chemical stability of the a8-FeCo phase, examination of alloy compositions, and developme...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Magnetics Society of Japan
سال: 1999
ISSN: 0285-0192
DOI: 10.3379/jmsjmag.23.225