Powder Metallurgy Processing and Characterization of the χ Phase Containing Multicomponent Al-Cr-Fe-Mn-Mo Alloy
نویسندگان
چکیده
High entropy alloys present many promising properties, such as high hardness or thermal stability, and can be candidates for applications. Powder metallurgy techniques enable the production of bulk with fine microstructures. This study aimed to investigate powder preparation, i.e., mechanical alloying sintering, non-equiatomic alloy from Al-Cr-Fe-Mn-Mo system. The structural microstructural investigations were performed on powders sample. indentation was carried out mechanically alloyed consists two bcc phases, one which is significantly predominant. annealed sample sintered at 950 °C 1 h consist a predominantly phase (71 ± 2 vol.%), an intermetallic χ (26 small volume fraction multielement carbides—M6C M23C6. presence carbides results carbon contamination balls vial during graphite die sintering. density 6.71 g/cm3 (98.4% relative density). presents very 948 34 HV1N Young’s modulus 245 8 GPa. showed possibility preparing ultra-hard multicomponent material reinforced by phase. research this system presented new knowledge formation in systems. Moreover, strengthening solid solution matrix via hard phases could interesting industrial
منابع مشابه
Phase Separation kinetics in Fe-Cr-Al alloy
9 The α α phase separation kinetics in a commercial Fe-20 wt% Cr-6% Al oxide dispersion-strengthened PM 1
متن کاملEffect of Density on the Microstructure and Mechanical Behavior of Powder Metallurgy Fe-mo-ni Steels
The microstructure and mechanical properties of Fe-0.85Mo-Ni powder metallurgy (P/M) steels were investigated as a function of sintered density. A quantitative analysis of microstructure was correlated with tensile and fatigue behavior to understand the influence of pore size, shape, and distribution on mechanical behavior. Tensile strength, Young’s modulus, strain-to-failure, and fatigue stren...
متن کاملVibrational properties of alpha- and sigma-phase Fe-Cr alloy.
Experimental and theoretical studies, of the Fe-partial phonon density of states (PDOS) for Fe52.5Cr47.5 alloy having alpha and sigma phases were carried out. The former using the nuclear resonant inelastic x-ray scattering method, and the latter with the direct one. Characteristic features of PDOS, which distinguish one phase from the other, were revealed and successfully reproduced by the the...
متن کاملAN INVESTIGATION ON ABRASIVE WEAR BEHAVIOUR OF Fe-C-Mo-FeCr COMPOSITE PRODUCED BY POWDER METALLURGY
In this study, the effect of chromium carbide (Cr7C3) on abrasive wear behavior of Fe-C-Mo-FeCr composite was investigated. Composite, which was produced by a powder metallurgy route was containing 3 wt.% Mo, 1.5 wt. % C and 4,8,12 wt. % FeCr with the different particle sizes. In the experiments, wear resistance of samples were determined using different loads by a pin on disc wear tester. Micr...
متن کاملSynthesis of Al2Ca Dispersoids by Powder Metallurgy Using a Mg–Al Alloy and CaO Particles
The elemental mixture of Mg-6 wt %Al-1 wt %Zn-0.3 wt %Mn (AZ61B) alloy powder and CaO particles was consolidated by an equal-channel angular bulk mechanical alloying (ECABMA) process to form a composite precursor. Subsequently, the precursor was subjected to a heat treatment to synthesize fine Al₂Ca particles via a solid-state reaction between the Mg-Al matrix and CaO additives. Scanning electr...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Alloys
سال: 2023
ISSN: ['2674-063X']
DOI: https://doi.org/10.3390/alloys2010003