Powder consolidation of Nd-Fe-B/α-Fe nanocomposite materials by cold deformation process
نویسندگان
چکیده
منابع مشابه
Sintering of Nd-Fe-B Magnets from Dy Coated Powder
High-coercive (Nd,Dy)-Fe-B magnets were fabricated via dysprosium coating on Nd-Fe-B powder. The sputtering coating process of Nd–Fe–B powder yielded samples with densities greater than 98%. (Nd,Dy)2Fe14B phases may have effectively penetrated into the boundaries between neighboring Nd2Fe14B grains during the sputtering coating process, thereby forming a (Nd,Dy)2Fe14B phase at the grain boundar...
متن کاملProduction of fine Nd-Fe-B alloy powder by pulsed plasma atomization
Extremely fine (<10 μm) Nd-Fe-B powder was generated by pulsed plasma atomization processing. The number average was just over 3 μm, as determined by computer-assisted scanning electron microscopy analysis of almost 3000 particles. Despite the fine particle size, alloys of stoichiometric Nd2Fe14B resulted in the properitectic formation of -Fe, deleteriously affecting the magnetic properties. N...
متن کاملRAPID COMMUNICATION Nanocomposite (Nd,Dy)(Fe,Co,Nb,B)5.5/α-Fe multilayer magnets with high performance
The structural and magnetic properties of rare-earth nanocomposite magnets of a (Nd,Dy)(Fe,Co,Nb,B)5.5 single layer and a (Nd,Dy)(Fe,Co,Nb,B)5.5/α-Fe multilayer prepared by sputtering and heat treatment have been investigated. Incomplete exchange coupling behaviour is observed in the Ti-buffered NdDyFeCoNbB + 40 wt%Fe single layer magnet. After annealing, the laminated nanostructure consisting ...
متن کاملSynthesis and liquid phase sintering of TiN/TiB2/Fe–Cr–Ni nanocomposite powder
Nanostructured TiN/TiB2/Fe–Cr–Ni composite powder has been prepared via high energy ball milling. Ti and BN powders are reacted to form uniform mixture of TiN and TiB2 within 2 h of milling by a mechanically activated self-sustaining reaction (MSR). The crystallite sizes of TiN nd TiB2 are about 7 and 16 nm, respectively, after 32 h of milling. Through liquid phase sintering and optimizing the ...
متن کاملCoercivity enhancement of Nd-Fe-B sintered magnets by grain boundary modification via reduction-diffusion process
The interface between the Nd2Fe14B particles and the grain boundary surrounding them in Nd-Fe-B sintered magnets was modified by diffusion Dy metal selectively through the grain boundary involving the reduction of Dy2O3 or DyF3 with CaH2 and the coercivity of them was effectively enhanced from 0.98 MA/m to 1.42 MA/m with keeping the high value of remanence. The resultant coercivity was higher t...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: AIP Advances
سال: 2018
ISSN: 2158-3226
DOI: 10.1063/1.5045797