Porous TiO2 Assembled from Monodispersed Nanoparticles
Porous TiO2 were assembled by evaporating or refluxing TiO2 colloid, which was obtained by dispersing the TiO2 nanoparticles with a crystallite size (d XRD) of 3.2 nm into water or ethanol without any additives. Porous transparent bulk TiO2 was obtained by evaporating the TiO2-C2H5OH colloid at room temperature for 2 weeks, while porous TiO2 nanospheres were assembled by refluxing the TiO2-H2O ...
متن کاملTiO2 and SnO2@TiO2 hollow spheres assembled from anatase TiO2 nanosheets with enhanced lithium storage properties.
TiO(2) and SnO(2)@TiO(2) hollow spheres assembled from anatase TiO(2) nanosheets with exposed (001) high-energy facets are constructed via a templating approach, and the as-prepared samples exhibit enhanced lithium storage properties.
متن کاملPolyol Process Synthesis of Monodispersed FePt Nanoparticles.
Monodispersed FePt nanoparticles are synthesized by reduction of iron(II) acetylacetonate and platinum(II) acetylacetonate with 1,2-hexadecanediol as the reducing reagent in the polyol process. As-prepared FePt nanoparticles are chemically disordered with fcc phase. Transmission electron microscopy (TEM) images show a self-assembled particle array with an average particle size of 3 nm and a sta...
متن کاملChemical Dynamics of Monodispersed Iron Oxide Nanoparticles
This study is comprised of the synthesis and characterization of uniform fine particles of iron oxide in different shapes and sizes. Varying amounts of iron (III) chloride and sodium dihydrogen phosphate was heated at 98 oC for various periods, following the forced hydrolysis method. Scanning electron microscopic analysis showed that the shape and size of the precipitated particl...
متن کاملAl2O3/TiO2 inverse opals from electrosprayed self-assembled templates
The fabrication of high optical quality inverse opals is challenging, requiring large size, three-dimensional ordered layers of high dielectric constant ratio. In this article, alumina/TiO2-air inverse opals with a 98.2% reflectivity peak at 798 nm having an area of 2 cm2 and a thickness of 17 µm are achieved using a sacrificial self-assembled structure of large thickness, which was produced wi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nanoscale Research Letters
سال: 2016
ISSN: 1931-7573,1556-276X
DOI: 10.1186/s11671-016-1372-2