Porous hydrogen substituted graphyne as a promising anode for lithium-ion batteries
نویسندگان
چکیده
منابع مشابه
Initial Discharge Capacity of Manganese Cobaltite as Anode Material for Lithium Ion Batteries
Nanostructured manganese cobalt oxide spinel (MnCo2O4) are prepared by co-precipitation method and calcined at 650 and 750°C. Morphological studies show that by increasing the calcination temperature from 650 to 750°C, morphology of the particles changes from quasi-plate to polyhedral. The MnCo2O4 calcined at 650°C could deliver an initial discharge capacity of 1438 mAh g-1 under current densit...
متن کاملBimetallic coordination polymer as a promising anode material for lithium-ion batteries.
Bimetallic coordination polymers (BiCPs) with Zn and Co were synthesized and applied as anode materials. When the rate was increased to 2 A g(-1), a capacity of 622 mA h g(-1) after 500 cycles could still be maintained.
متن کاملSurface‐Amorphous and Oxygen‐Deficient Li3VO4−δ as a Promising Anode Material for Lithium‐Ion Batteries
Surface-amorphous and oxygen-deficient Li3VO4-δsynthesized by simple annealing of Li3VO4 powders in a vacuum shows great enhancements in both reversible capacity and coulombic efficiency for the first discharge/charge without delicate size control and carbon coating. The results are associated with the improved charge-transfer kinetics caused by the amorphous surface of Li3VO4-δ .
متن کاملElectrochemical Evaluation of PbO Nanoparticles as Anode for Lithium Ion Batteries (Technical Note)
PbO nanoparticles were synthesized using hydrothermal process. Scanning electron microscopy (SEM) was used in order to investigate of PbO powders. X-ray diffraction (XRD) pattern confirmed β-PbO formation during this process. The crystallite size of the powders was calculated using Scherrer formula about 74.6 nm. Electrochemical evaluation of the PbO nanoparticles as anode for Li-ion batteries ...
متن کاملSynthesis of Hard Carbon- Silicon Nanocomposite as Anode Active Material for Lithium-Ion Batteries
In this research, using phenolic resin as the precursor of carbon and various amounts of ethylene glycol as a pore former, porous samples of hard carbon were synthesized. Samples were characterized by x-ray diffraction (XRD) and N2 adsorption-desorption methods. Broad diffraction peaks represent the amorphous structure of samples. Moreover, the gas adsorption-desorption curves showed that the a...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: RSC Advances
سال: 2021
ISSN: 2046-2069
DOI: 10.1039/d1ra03396d