Porosity development during steam activation of carbon foams from chemically modified pitch
نویسندگان
چکیده
منابع مشابه
Carbon Foam Production from a Thermo- Chemically Modified Commercial Coal Tar Pitch
Introduction The unique properties of carbon foam mainly depend on the precursor features and synthesis conditions. For the highly thermal and electrical conductive carbon foam, an anisotropic pitch precursor is required [1, 2]. A lot of factors influence the foaming process, but temperature and pressure are the most critical aspects [3]. The aim of the present investigations is to adjust by ap...
متن کاملPorosity Evolution of Activated Carbon Fiber Prepared from Liquefied Wood. Part I: Water Steam Activation at 650 to 800 °C
Activated carbon fiber is known as an excellent adsorbent material due to its well-developed pore structure. In this work, the porosity evolution of activated carbon fiber prepared from phenol liquefied wood with water steam activation at 650 to 800 °C for 20 to 260 min was examined by physical adsorption of N2 at -196 °C. By the series of activation processes, the specific surface area and por...
متن کاملChemically modified activated carbon with ethylenediamine for
Carbon active chemically bonded ethylenediamine as one sorbents successfully were applied for the enrichment of trace amount of some metal ions. The influences of the variables including pH, amount of solid phase, sample flow rate, type and condition of eluting solution and sample volume on the metal ions recoveries were investigated. The method has high sorption-preconcentration efficiency eve...
متن کاملMicroporosity Development in Coal-Based Carbon Foams
This paper presents a novel method of manufacturing carbon foams from coals with a bimodal porosity structure (macroand microporosity), by means of a carbonisation process at 450 or 475 °C that produces the carbon foam, followed by chemical activation with zinc chloride at 500 °C. The activation agent influences the development of macroporosity during the foaming step and gives rise to micropor...
متن کاملDevelopment of pH Sensitive Nanoparticles for Intestinal Drug Delivery Using Chemically Modified Guar Gum Co-Polymer
The aim of the research work was to chemically modify guar gum(GG) as a pH sensitive co-polymer and formulating intestinal targeting ESO nanoparticles (NPs) using the synthesized co-polymer. Poly acrylamide-grafted-guar gum (PAAm-g-GG) co-polymer was synthesized by free radical polymerization. Chemical modification of PAAm-g-GG by alkaline hydrolysis results in formation of a pH-sensitive co-po...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Microporous and Mesoporous Materials
سال: 2012
ISSN: 1387-1811
DOI: 10.1016/j.micromeso.2011.08.023