Polystyrene latex particles coated with crosslinked poly(N-isopropylacrylamide)
نویسندگان
چکیده
منابع مشابه
Polystyrene latex particles coated with crosslinked poly(N-isopropylacrylamide)
Thermoresponsive colloidal particles were prepared by seeded precipitation polymerization of N-isopropylacrylamide (NIPAM) in the presence of a crosslinking monomer, N,N-methylenebisacrylamide (MBA), using polystyrene latex particles (ca. 50 nm in diameter) as seeds in aqueous dispersion. Phase transitions of the prepared poly(N-isopropylacrylamide), PNIPAM, shells on polystyrene cores were stu...
متن کاملPreparation of Silver - Coated Polystyrene Composite Particles
We report a feasible approach to the preparation of monodispersed metal-shell composite microspheres based on a combination of surface reaction and surface seeding techniques. The method was implemented for coating polystyrene (PS) spheres with silver shell having a variable thickness by controlling the amount of reagents in the reaction procedure. These composite spherical particles in dimensi...
متن کاملElectrokinetic behavior and colloidal stability of polystyrene latex coated with ionic surfactants.
This work is focused on analyzing the electrokinetic behavior and colloidal stability of latex dispersions having different amounts of adsorbed ionic surfactants. The effects of the surface charge sign and value, and the type of ionic surfactant were examined. The analysis of the electrophoretic mobility (mu(e)) versus the electrolyte concentration up to really high amounts of salt, much higher...
متن کاملVoltammetric discrete current of polyaniline-coated latex particles at microelectrodes
Suspensions of polyaniline-coated latex particles 13 μm in diameter showed the integer-fold voltammetric currents at the microelectrode of which size was similar to the diameter of the particles. The currents did not vary with concentrations of polyaniline particles but varied accidentally with each voltammetric run. They were caused by the reduction of a few polyaniline particles adsorbed on t...
متن کاملDesign of polystyrene latex particles covered with polyoxometalate clusters via multiple covalent bonding.
Polyoxometalates (POMs) covalently functionalized with methyl methacrylate groups were applied as surfactants in the emulsion polymerization reaction of styrene. Due to the copolymerization of the methyl methacrylate groups and the styrene monomers, the polyoxometalate clusters are covalently grafted onto the surface of polystyrene latex nanoparticles. Such latex particles are fully covered wit...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Colloid and Polymer Science
سال: 2006
ISSN: 0303-402X,1435-1536
DOI: 10.1007/s00396-006-1470-2