Polymerization Shrinkage and Degree of Conversion of New Zirconia-Reinforced Rice Husk Nanohybrid Composite
نویسندگان
چکیده
منابع مشابه
Volumetric Polymerization Shrinkage of Contemporary Composite Resins
The polymerization shrinkage of composite resins may affect negatively the clinical outcome of the restoration. Extensive research has been carried out to develop new formulations of composite resins in order to provide good handling characteristics and some dimensional stability during polymerization. The purpose of this study was to analyze, in vitro, the magnitude of the volumetric polymeriz...
متن کاملPolymerization shrinkage of dental composite resins.
Aesthetic materials have always been a priority for the restoration of anterior teeth; increasingly, they have also gained prominence in the restoration of posterior teeth. This has been due to their advantages as an alternative to amalgam. Their drawbacks however, can include poor marginal adaptation, postoperative sensitivity and cuspal movement. These are particularly associated with the pol...
متن کاملEffect of Shade on Immediate and Post-Curing Polymerization Shrinkage of Composite Resin
Background and Aim: Minimizing the polymerization shrinkage of composite resins is a critical goals in composite restorations. Many factors affect polymerization shrinkage. This study aimed to evaluate the effect of composite resin shade on polymerization shrinkage. Materials and Methods: In this in vitro study, 14 composite discs measuring 1.5×8 mm were fabricated. The samples were prepared u...
متن کاملMarine Durability Characteristics of Rice Husk Ash-Modified Reinforced Concrete
This paper addresses the potential use of Rice Husk Ash (RHA) as a cementitious material in concrete mixes. RHA is produced from the burning of rice husk which is a byproduct of rice milling. The ash content is about 18-22% by weight of the rice husks. Research has shown that concrete made with RHA as a partial cement substitute to levels of 10% to 20% by weight of cement has superior performan...
متن کاملShrinkage stress and degree of conversion of a dental composite submitted to different photoactivation protocols.
The aim of this study was to evaluate the polymerization stress and degree of conversion of a composite submitted to different photoactivation protocols. The composite Filtek Z350 was placed in the central perforation of a photoelastic disc and polymerized using a LED-based curing unit (BluePhase II--Ivoclar Vivadent) with energy density of 12, 24 or 36 J/cm2 using the following photopolymeriza...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: European Journal of Dentistry
سال: 2020
ISSN: 1305-7456,1305-7464
DOI: 10.1055/s-0040-1713951