Polymerization Characteristics of EMA-Based Resin
نویسندگان
چکیده
منابع مشابه
Polymerization characteristics of ethyl methacrylate-based resin initiated by TBB.
Polymerization characteristics of 4 types of ethyl methacrylate (EMA)-based resin, composed of EMA and EMA/methyl methacrylate (MMA) copolymers and initiated by tributylborane (TBB), were studied from the aspects of long term changes of residual monomer (RM) and molecular weight (Mw). The resins were polymerized at room temperature for 30 min, stored at 37 degrees C for 24 hr, 1 and 4 weeks and...
متن کاملThe effect of resin thickness on polymerization characteristics of silorane-based composite resin
OBJECTIVES This study examined the influence of the resin thickness on the polymerization of silorane- and methacrylate-based composites. MATERIALS AND METHODS One silorane-based (Filtek P90, 3M ESPE) and two methacrylate-based (Filtek Z250 and Z350, 3M ESPE) composite resins were used. The number of photons were detected using a photodiode detector at the different thicknesses (thickness, 1,...
متن کاملNanoindentation tests to assess polymerization of resin-based luting cement.
OBJECTIVE The optimal polymerization of resin-based luting cements plays a critical role in the long-term clinical success of dental prostheses and indirect restorations. This study investigated a mutual action between the conformational changes and mechanical properties of a dimethacrylate resin-based luting cement with and without pre-application of the acidic functional monomer 10-methacrylo...
متن کاملDevelopment of an orthodontic elastic material using EMA-based resin combined with 1-butanol.
For the development of new orthodontic elastic material, 1-butanol was added to PEMA-TA/HX resin. In the present study, basic experiments to reveal the mechanical properties of the materials were conducted. FT-IR spectroscopy showed that addition of 1-butanol did not cause any chemical changes to the PEMA-TA/HX resin. After addition of 1-butanol to PEMA-TA/HX resin, the modulus of elasticity, i...
متن کاملEffect of Shade on Immediate and Post-Curing Polymerization Shrinkage of Composite Resin
Background and Aim: Minimizing the polymerization shrinkage of composite resins is a critical goals in composite restorations. Many factors affect polymerization shrinkage. This study aimed to evaluate the effect of composite resin shade on polymerization shrinkage. Materials and Methods: In this in vitro study, 14 composite discs measuring 1.5×8 mm were fabricated. The samples were prepared u...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Dental Materials Journal
سال: 2004
ISSN: 1881-1361,0287-4547
DOI: 10.4012/dmj.23.14