Polymer Stabilized Metal Nanoparticles for Catalytic Degradation of Methylene Blue in Water

Methylene blue is highly toxic and releases from various industries. It must be transformed into less compounds. The Core-Shell microgels p (Pst core), Pstcore-NIPMamm-MAa Ag in Pst-p NIPMamm-MAa have been synthesized using the hybrid micro gelling emulsion polymerization process. 0.086mM, MB 6.2mM NaBH4 0.2916 mg / mL catalysts cuvette were measured UV-visible spectrophotometers. Spectrums at a one-minute interval. peak 600 nm steadily decreased over time was completely eliminated after 11 minutes. Without catalyst, decreases with which showed that reaction slow very high within 120 Psty core of FT-IR microgels, pNIpmam-MMAA, Ag-pNIpmam-MAA are hybrids. At 2955 2845 cm−1 spectra, NiPMaM – MaA Ag-p used for shell C-H vibrations expanding aromatic ring. In this study degradation carried out Ag- Nanocomposites different interval to check minimum time. dye