Polaronic interactions between oxygen vacancies in rutile TiO2
نویسندگان
چکیده
منابع مشابه
Bonding of gold nanoclusters to oxygen vacancies on rutile TiO2(110).
Through an interplay between scanning tunneling microscopy (STM) and density functional theory (DFT) calculations, we show that bridging oxygen vacancies are the active nucleation sites for Au clusters on the rutile TiO2(110) surface. We find that a direct correlation exists between a decrease in density of vacancies and the amount of Au deposited. From the DFT calculations we find that the oxy...
متن کاملInterplay between Steps and Oxygen Vacancies on Curved TiO2(110).
A vicinal rutile TiO2(110) crystal with a smooth variation of atomic steps parallel to the [1-10] direction was analyzed locally with STM and ARPES. The step edge morphology changes across the samples, from [1-11] zigzag faceting to straight [1-10] steps. A step-bunching phase is attributed to an optimal (110) terrace width, where all bridge-bonded O atom vacancies (Obr vacs) vanish. The [1-10]...
متن کاملInteraction of CO2 with oxygen adatoms on rutile TiO2(110).
The interactions of CO2 with oxygen adatoms (Oa's) on rutile TiO2(110) surfaces have been studied using scanning tunneling microscopy. At 50 K CO2 is found to adsorb preferentially on five-coordinated Ti sites (Ti5c's) next to Oa's rather than on oxygen vacancies (VO's) (the most stable adsorption sites on reduced TiO2(110)). Temperature dependent studies show that after annealing to 100-160 K,...
متن کاملDefective TiO2 with oxygen vacancies: synthesis, properties and photocatalytic applications.
Titanium dioxide (TiO2), as an important semiconductor metal oxide, has been widely investigated in the field of photocatalysis. The properties of TiO2, including its light absorption, charge transport and surface adsorption, are closely related to its defect disorder, which in turn plays a significant role in the photocatalytic performance of TiO2. Among all the defects identified in TiO2, oxy...
متن کاملThe interplay between dopants and oxygen vacancies in the magnetism of V-doped TiO2.
Density functional theory calculations indicate that the incorporation of V into Ti lattice positions of rutile TiO(2) leads to magnetic V(4+) species, but the extension and sign of the coupling between dopant moments confirm that ferromagnetic order cannot be reached via low-concentration doping in the non-defective oxide. Oxygen vacancies can introduce additional magnetic centres, and we show...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Physical Review B
سال: 2017
ISSN: 2469-9950,2469-9969
DOI: 10.1103/physrevb.95.054104