Plastic Working. Low Temperature Drawing Technique of Magnesium Alloy AZ31.

Mechanisms of Plastic Deformation in AZ31 Magnesium Alloy Investigated by Acoustic Emission and Electron Microscopy

Effect of Temperature on Diffusion-Bonded Joint of AZ31 Magnesium and 7075 Aluminum Alloy

In this study, the effect of temperature on the diffusion welding of AZ31 magnesium alloy and 7075 aluminum was discussed. Diffusion welding temperature was the most important parameter since all mechanisms are sensitive to temperature in Diffusion welding method. Intrusive contacts between the two alloys at temperatures of 430, and 440 °C 450 and took 60 min. In all tests constant pressure and...

Effect of Temperature on Diffusion-Bonded Joint of AZ31 Magnesium and 7075 Aluminum Alloy

In this study, the effect of temperature on the diffusion welding of AZ31 magnesium alloy and 7075 aluminum was discussed. Diffusion welding temperature was the most important parameter since all mechanisms are sensitive to temperature in Diffusion welding method. Intrusive contacts between the two alloys at temperatures of 430, and 440 °C 450 and took 60 min. In all tests constant pressure and...

Anodizing of Magnesium Alloy Az31 by Alkaline Solution

-Anodizing of AZ 31 Mg alloy was investigate in 3M KOH solution for 10, 20 and 30min. at constant voltage of 5V. Atomic force microscope (AFM) used to investigate the roughness of anodic film formed on the surface while the scanning electron microscope (SEM) was used to determine the morphology of the anodic film, it was found that the roughness of the anodic film is mainly depend on the anodiz...

Corrosion Behavior of the Friction Stir Welded AZ31 Magnesium Alloy.

* IDMEC, Instituto Superior Técnico, Universidade de Lisboa, Av. Rovisco Pais, 1049-001 Lisboa, Portugal ** DEQ/ICEMS, Instituto Superior Técnico, Universidade de Lisboa, Av. Rovisco Pais, 1049001 Lisboa, Portugal. *** Department of Engineering Design and Production, School of Engineering, Aalto University, P.O. Box 1420, FI-00076 Aalto, Finland **** Faculdade de Engenharia da universidade do P...