Plasma Electrolytic Oxidation of Binary Al-Sn Alloys
نویسندگان
چکیده
منابع مشابه
Process Monitoring of Plasma Electrolytic Oxidation
Plasma electrolytic oxidation (PEO) is a potential technique to coat a dense ceramic oxide layer on the surface of light metals, e.g. Al, Mg or Ti. In our PEO process, Al-pieces are emerged in aqueous solutions containing dissolved silicate/alkali, e.g. KOH/NaOH and K 2 SiO 3 /Na 2 SiO 3. Using a DC-pulsed system with 20Hz, micro-arcs are induced at the surface of the pieces randomly and plasma...
متن کاملOsseointegration improvement by plasma electrolytic oxidation of modified titanium alloys surfaces.
Titanium (Ti) is a material frequently used in orthopedic applications, due to its good mechanical properties and high corrosion resistance. However, formation of a non-adherent fibrous tissue between material and bone drastically could affect the osseointegration process and, therefore, the mechanical stability of the implant. Modifications of topography and configuration of the tissue/materia...
متن کاملPlasma Electrolytic Oxidation Coatings on Lightweight Metals
Lightweight metals, e.g. aluminum (Al), magnesium (Mg), titanium (Ti) and their alloys are of great importance for applications in various machinery and transportation system, espe‐ cially in aerospace and automobile products due to their high strength-to-weight ratio and superior physical and chemical performances. However, their poor tribological properties, such as low wear resistance, high ...
متن کاملEnhanced Compressive Property of Al Composite Foams at Elevated Temperatures via Plasma Electrolytic Oxidation
The present work investigates the compressive property of Al matrix composite foams at different temperatures between room temperature and 200 ◦C. Elevated temperature results in a decreased compressive strength and energy absorption capacity of as-received Al foams. Therefore, to maintain the compressive property, the Al2O3 ceramic coating was deposited on the Al struts of the foams by the pla...
متن کاملOxidation – Nitridation of Ni-Cr-Al Alloys
A series of alloys containing 24-36 wt pct Cr and 13.5 – 25.0 wt pct Al was reacted with air at 1100 °C for 260 h. The products of isothermal reaction were scales of α-Al 2 O 3 plus small amounts of Cr 2 O 3 . These grew according to parabolic kinetics, interrupted by episodic weight losses caused by partial spallation. No nitridation occurred during the isothermal exposures. Reaction during th...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Physica Polonica A
سال: 2014
ISSN: 0587-4246,1898-794X
DOI: 10.12693/aphyspola.125.659