Physical properties and hydration evolution of dispersant containing calcium aluminate cement compositions for endodontic applications
نویسندگان
چکیده
منابع مشابه
Physical properties and hydration evolution of dispersant containing calcium aluminate cement compositions for endodontic applications (Propriedades físicas e evolução da hidratação de composições de cimento de aluminato de cálcio contendo dispersante para aplicações endodônticas)
The purpose of this study was to evaluate the physical properties and hydration evolution of calcium aluminate cement (CAC) compositions containing an advanced dispersant. The compressive strength, dimensional change, apparent porosity and quantitative X ray diffraction analysis (XRD) of the cement pastes were carried out over 1-15 days of curing (with the samples immersed in distilled water) a...
متن کاملPremixed calcium silicate cement for endodontic applications
Calcium silicate-based materials (also called MTA) are increasingly being used in endodontic applications. However, the handling properties of MTA are not optimal when it comes to injectability and cohesion. Premixing the cements using glycerol avoids these issues. However, there is a lack of data on the effect of common cement variables on important properties of premixed cements for endodonti...
متن کاملThe Hydration Products of a Refractory Calcium Aluminate Cement at Low Temperatures
Calcium aluminates (CA) are the most important hydraulically setting cements used for preparing refractory castables, because they develop high strength at very early ages after placements. The anhydrous phases of this kind of cements are CA, CA2 and traces of C12A7 and alpha-alumina. The major hydraulic phase in all of the CA cements including ciment fondu...
متن کاملThe Hydration Products of a Refractory Calcium Aluminate Cement at Intermediate Temperatures
The major hydraulic phase in all the calcium aluminate cements including ciment fondue is CA (CaAl2O4). Once hydrated, it starts to form the hexagonal crystals of CAH10 and C2AH8 that depending on the time and temperature of hydration convert to the cubic crystals of C3AH6 and AH3. The nature, sequence, ...
متن کاملInvestigation of the effect of phosphate on the physical and microstructural properties of synthetic calcium aluminate cement
The aim of this study was to investigate the synthesis of calcium aluminate cement with and without phosphate additive by combustion synthesis. After preparing the gel from a solution containing aluminum and calcium nitrates and glycine fuel and ammonium dihydrogen Phosphate, its combustion was performed at 400 ° C. X-ray diffraction pattern and thermal analysis of the combustion sample showed...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Cerâmica
سال: 2014
ISSN: 0366-6913
DOI: 10.1590/s0366-69132014000300007