Photocatalytic reduction of methylene blue by TiO2 nanotube arrays: effects of TiO2 crystalline phase
نویسندگان
چکیده
منابع مشابه
Photocatalytic reduction of methylene blue by TiO2 nanotube arrays: effects of TiO2 crystalline phase
TiO2 nanotube arrays were synthesized by anodization of Ti metal sheets followed by thermal annealing at elevated temperatures from 400 to 600 C. Scanning electron microscopic measurements showed that dense arrays of nanotubes were produced with the inner diameter about 100 nm, wall thickness 35 nm, and length about 10 lm. X-ray diffraction measurements showed that the as-prepared nanotubes wer...
متن کاملStructural manipulation of the photocatalytic activity of TiO2 nanotube arrays
Highly ordered TiO2 nanotube arrays on Ti substrates were prepared by an electrochemical anodization process in a mixture of glycerol and water containing 0.5 wt% NH4F and then thermally annealed from 400 C to 600 C. The sample structures were characterized by scanning electron microscopy and X-ray diffraction measurements, where the nanotube pore diameter and length were found to increase with...
متن کاملKinetics of photocatalytic degradation of methylene blue on nanostructured TiO2 coatings created by sol-gel process
Sol-gel process was chosen to produce a photocatalytic film to degrade methylene blue. In order to study structural and morphological properties of the coatings, a base sol of TTIP, I-PrOH, and DEA was prepared. Then with addition of 45g/L PEG 2000, 30g/L TiO2 and 15g/L PEG 2000 + 30g/L TiO2, to the base sol, three other sols were produced. The results of this study indica...
متن کاملComposite of TiO2-montmorillonite from Indonesia and Its photocatalytic Properties in Methylene Blue and E.coli Reduction
Titania pillared montmorillonite from Indonesian montmorillonite by using titanium isopropoxide as precursor was successfully prepared. Physico-chemical character of material by using x-ray diffraction, gas sorption analyzer, diffuse reflectance UV-Visible, scanning electron microscope (SEM) and energy dispersive x-ray (EDAX) showed the dipersion of titania in dominantly anatase phase that is t...
متن کاملPhotocatalytic methane decomposition over vertically aligned transparent TiO2 nanotube arrays.
We report here on a study of vertically aligned TiO(2) nanotube arrays grown by the one-step anodic oxidation technique and their photocatalytic performance for methane decomposition. Quantitative activity data as a function of film thickness is obtained.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Materials Science
سال: 2010
ISSN: 0022-2461,1573-4803
DOI: 10.1007/s10853-010-4254-5