Photocatalytic degradation of acetic acid on spinel ferrites MFe2O4 (M= Mg, Zn, and Cd)
نویسندگان
چکیده
منابع مشابه
GAS SENSING PROPERTIES OF POROUS Cu-, Cd- AND Zn- FERRITES
Some spinel ferrites, MFe2O4 (M = Cu, Cd and Zn), having submicron grain sizes (0.1–0.7μm) were prepared by sol-gel-selfcombustion and their sensing properties to reducing gases were investigated. The gas sensing characteristics were obtained by measuring the sensitivity as a function of various controlling factors, like operating temperature, composition and concentration of the gas, and final...
متن کاملPhotocatalytic dye degradation properties of Zinc Copper Ferrites nanoparticles
In the present study, new multi-components spinel ferrite Zinc doped metallic ferrites are investigated. The synthesized compounds consisting of Zinc copper ferrite nanostructures were developed using the Co-precipitation technique. Powder X-ray diffraction pattern (XRD) confirms the formation of the spinel phase for all the samples. The lattice constant was studied through powder X-ray diffrac...
متن کاملEnhanced photoelectrochemical and photocatalytic behaviors of MFe2O4 (M = Ni, Co, Zn and Sr) modified TiO2 nanorod arrays
Modified TiO2 nanomaterials are considered to be promising in energy conversion and ferrites modification may be one of the most efficient modifications. In this research, various ferrites, incorporated with various cations (MFe2O4, M = Ni, Co, Zn, and Sr), are utilized to modify the well aligned TiO2 nanorod arrays (NRAs), which is synthesized by hydrothermal method. It is found that all MFe2O...
متن کاملPreparation and Ethanol Sensing Behavior of Spinel-type Nanosized Mixed Ferrites Containing Zn
Nanocrystalline Ni1-xZnxFe2O4 (x = 0, 0.2, 0.3 and 0.4) mixed ferrite with cubic spinel structure was successfully prepared by the citrated sol-gel method followed by calcinations at 600 C. Characterization of the materials was performed by XRD. Indirect-heating sensors using as-prepared powders of mixed ferrite as sensitive materials were fabricated on an alumina tube with Au electrodes and Pl...
متن کاملIn Vitro Degradation Behavior of Ternary Mg-Zn-Se and Mg-Zn-Cu Alloys as Biomaterials.
In this study, the corrosion behavior of Mg-Zn-Se and Mg-Zn-Cu alloys was investigated to evaluate their corrosion behavior related to use as implantable biomaterials. The corrosion behavior of these alloys and a commercially available Mg-Zn alloy were examined using static solution electrochemical testing, dynamic solution gravimetric testing, ion leaching testing, and microscopic evaluation. ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Catalysis Communications
سال: 2014
ISSN: 1566-7367
DOI: 10.1016/j.catcom.2014.01.016