Phosphate adsorption onto thermally dehydrated aluminate cement granules

نویسندگان
چکیده

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Preparation of porous apatite granules from calcium phosphate cement.

A versatile method for preparing spherical, micro- and macroporous (micro: 2-10 and macro: 150-550 microm pores), carbonated apatitic calcium phosphate (Ap-CaP) granules (2-4 mm in size) was developed by using NaCl crystals as the porogen. The entire granule production was performed between 21 and 37 degrees C. A CaP cement powder, comprising alpha-Ca3(PO4)2 (61 wt.%), CaHPO4 (26%), CaCO3 (10%)...

متن کامل

Aluminate Cement (EndoBinder) Containing Different Radiopacifiers

containing different radiopacifiers, Bi2O3, ZnO or ZrO2, compared with Mineral Trioxide Aggregate (MTA). According to ISO 10993-12:2012 (E) recommendations, 0.2 g of each cement were applied in transwell inserts and placed in 24-well culture plates containing 1 mL of culture medium (DMEM). After 24 h of incubation, the extracts (DMEM containing components released from the cements) were applied...

متن کامل

Development and characterization of α-tricalcium phosphate/monocalcium aluminate composite bone cement

Calcium phosphate cements have received much attention in recent decades owing to their biocompatibility, in situ handling, and shaping abilities. However, their low initial mechanical strength is still a major limitation. On the other hand, calcium aluminate cements (CACs) set fast and have a high initial strength and good corrosion resistance in contact with body fluids, making them excellent...

متن کامل

Formation of copper aluminate spinel and cuprous aluminate delafossite to thermally stabilize simulated copper-laden sludge.

The study reported herein indicated the stabilization mechanisms at work when copper-laden sludge is thermally treated with gamma-alumina and kaolinite precursors, and evaluated the prolonged leachability of their product phases. Four copper-containing phases - copper oxide (CuO), cuprous oxide (Cu(2)O), copper aluminate spinel (CuAl(2)O(4)), and cuprous aluminate delafossite (CuAlO(2)) - were ...

متن کامل

Investigation of the effect of phosphate on the physical and microstructural properties of synthetic calcium aluminate cement

The aim of this study was to investigate the synthesis of calcium aluminate cement with and without phosphate additive by combustion synthesis. After preparing the gel from a solution containing aluminum and calcium nitrates and glycine fuel and ammonium dihydrogen Phosphate, its combustion was performed at 400 ° C.  X-ray diffraction pattern and thermal analysis of the combustion sample showed...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: RSC Advances

سال: 2018

ISSN: 2046-2069

DOI: 10.1039/c8ra02474j