Phase selection and nanocrystallization in Cu-free soft magnetic FeSiNbB amorphous alloy upon rapid annealing
نویسندگان
چکیده
منابع مشابه
Nanocrystallization in Co67Cr7Fe4Si8B14 Amorphous Alloy Ribbons
The nanocrystallization of Co67Fe4Cr7Si8B14 amorphous ribbons which prepared by planar flow melt spinning process (PFMS) was investigated. Crystallization of the ribbons was studied by differential thermal analysis (DTA), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The DTA result of amorphous ribbon at heating rate of 10˚C/min showedoccurrence of phase transitions in two...
متن کاملnanocrystallization in co67cr7fe4si8b14 amorphous alloy ribbons
the nanocrystallization of co67fe4cr7si8b14 amorphous ribbons which prepared by planar flow melt spinning process (pfms) was investigated. crystallization of the ribbons was studied by differential thermal analysis (dta), x-ray diffraction (xrd) and transmission electron microscopy (tem). the dta result of amorphous ribbon at heating rate of 10˚c/min showedoccurrence of phase transitions in two...
متن کاملKINETICS OF -Fe NANOCRYSTALLIZATION IN Fe55Cr18Mo7B16C4 BULK AMORPHOUS ALLOY
Abstract: In this research work, crystallization kinetics of Fe55Cr18Mo7B16C4 alloy was evaluated by X-ray diffraction, TEM observations and differential scanning calorimetric tests. In practice, crystallization and growth mechanisms were investigated using DSC tests in four different heating rates. Results showed that a two -step crystallization process occurred in the alloy in which - Fe phas...
متن کاملEffect of Cu Addition on Soft Magnetic Properties of Fe–Zr–Si Amorphous Alloy
The effect of Cu addition on the soft magnetic properties of FeZrSi amorphous alloy was investigated by X-ray analysis, TEM observation, and B-H curve tracer. As a melt-spun amorphous ribbon sample was annealed above the crystallization onset temperature, very fine ¡-Fe particles smaller than 315 nm were precipitated and uniformly distributed in an amorphous matrix. Cu addition to FeZrSi am...
متن کاملEffect of P addition on nanocrystallization and high temperature magnetic properties of low B and Nb containing FeCo nanocomposites
The P content dependencies of the nanocrystallization behaviors and high temperature magnetic properties of the Fe 54.6 Co 29.4 Si 2.8 (B 0.8ÀY P Y) 14 Nb 1 Cu 1 (Y ¼ 0, 0.2, and 0.3) alloys have been investigated. Alloys were prepared by melt spinning and subsequently annealed in an argon atmosphere to induce nanocrystallization. P addition increases primary crystallization temperature (Tx 1),...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Applied Physics
سال: 2016
ISSN: 0021-8979,1089-7550
DOI: 10.1063/1.4944595