PHASE COMPOSITION AND OXIDATION DEGREE OF VANADIUM IN CATALYSTS FOR OXIDATIVE DEHYDROGENATION OF PROPANE

نویسندگان

چکیده

The phase composition of vanadium and vanadium-antimony-containing samples γ-Al2O3 the degree oxidation in them were examined by XRD EPR methods, respectively. data spectroscopy show formation highly dispersed vanadium-oxygen vanadiumantimony-oxygen structures on surface support. It is shown that spectra studied are due to "isolated" ions with an state +4 nonstoichiometric vanadium-antimony-oxygen formations a square pyramid local environment structure characteristic V=O double bond. two types paramagnetic centers vanadium, which differ distortion square-pyramidal ion, identified. was established number V,Sb-containing depends V/Sb ratio them.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Structure and Properties of Vanadium Oxide–Zirconia Catalysts for Propane Oxidative Dehydrogenation

The structure of vanadia species supported on zirconia depends on VOx surface density and on the temperature of catalyst oxidation pretreatments. X-ray diffraction and Raman and UV-visible spectroscopies show that supported VOx species form polyvanadate domains of increasing size and ultimately monolayers and clusters as vanadium surface density increases. Initial propene selectivities in oxida...

متن کامل

Vanadium Oxide Supported on Al-modified Titania Nanotubes for Oxidative Dehydrogenation of Propane

In this study, characterization of vanadia supported on Al-modified titania nanotubes (TiNTs) synthesized by the alkaline hydrothermal treatment of TiO2 powders has been reported. A promising catalyst for oxidative dehydrogenation (ODH) of propane was prepared via the incipient wetness impregnation method. The morphology and crystalline structure of TiNTs were characterized by transmission elec...

متن کامل

Anomalous reactivity of supported V2O5 nanoparticles for propane oxidative dehydrogenation: influence of the vanadium oxide precursor.

The oxidative dehydrogenation (ODH) of propane to propylene by supported vanadia catalysts has received much attention in recent years, but different reactivity trends have been reported for this catalytic reaction system. In the present investigation, the origin of these differing trends are investigated with synthesis of supported V/SiO2, V/TiO2, and V/Al2O3 catalysts prepared with three diff...

متن کامل

Catalytic Properties of Supported MoO3 Catalysts for Oxidative Dehydrogenation of Propane

The effects of MoOx structure on propane oxidative dehydrogenation (ODH) rates and selectivity were examined on Al2O3-supported MoOx catalysts with a wide range of surface density (0.4-12 Mo/nm), and compared with those obtained on MoOx/ZrO2. On MoOx/Al2O3 catalysts, propane turnover rate increased with increasing Mo surface density and reached a maximum value for samples with ~ 4.5 Mo/nm. All ...

متن کامل

Synthesis of Three-Dimensionally Ordered Macroporous NiCe Catalysts for Oxidative Dehydrogenation of Propane to Propene

Three-dimensionally ordered macroporous (3DOM) NiCe catalysts with different Ni/Ce molar ratio were fabricated using the colloidal crystal templating method. The physic-chemical properties of the samples were characterized by various techniques, including N2 adsorption–desorption, X-ray diffraction (XRD), transmission electron microscopy (TEM), Raman, and H2-temperature-programmed reduction (TP...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Kimya probleml?ri

سال: 2022

ISSN: ['2221-8688', '2522-1655']

DOI: https://doi.org/10.32737/2221-8688-2022-3-358-365