Phase and properties prediction of Al–Ag binary system using thermo-calc

Abstract The temperature phase diagram stability and physical properties of a binary Silver–Aluminium (Al–Ag) alloy system have been calculated using Thermo-Calc 2021b software at range 250–1300 K. Six single-solid phases other than the liquid phase, elemental Ag (fcc_Ag), Al (fcc_Al), hcp_A3, cub_A13, bcc_Ag were obtained from equilibrium calculation. Ten regions double evaluated. Three intermediate also with five invariant reactions, namely one eutectic reaction (at 840.00 K), two peritectic reactions 1051.22 K 1003.18 peritectoid 730.58 881.40 K) equally found. Sixteen 0, 100, respectively, obtained. Maximum solid solubility was 5.60 mass percent 730. 58 for in 58.17 Al. From temperature–composition diagram, melting point pure silver aluminium inferred as 1234.96 933.50 K, which agrees experimental standards. These results play significant role processing Al–Ag different industrial-related applications. Graphical abstract