Pembentukan Fasa dan Suhu Genting Superkonduktor (Tl0.5Pb0.5)Sr2Ca(Cu2-xCrx)O7-δ (x = 0 - 0.100)

نویسندگان

چکیده

Superkonduktor fasa (Tl0.5Pb0.5)Sr2Ca(Cu2-xCrx)O7-δ (Tl-1212) bagi x = 0 hingga 0.100 telah disediakan menggunakan kaedah tindak balas keadaan pepejal. Tujuan kajian ini ialah menentukan suhu optimum untuk pembentukan Tl-1212 dengan komposisi ini. Sampel dalam aliran gas oksigen tiga berlainan iaitu 850 °C kerajang perak selama 5 jam, dan 950 1000 4 min. Bahan diciri pembelauan sinar-X mengenal pasti pengukuran rintangan elektrik (R) genting. yang dipanaskan pada menunjukkan pecahan isi padu tertinggi (94% 0). genting mula, Tc mula 102 K. Terbitan melawan (T), dR/dT sampel (x 0.015 - 0.100) mempunyai puncak hampir sama Tp1 Tp2. Ini kesuperkonduksian intrabutiran (Tp1) antara butiran (Tp2) berlaku adalah sama. Hasil pemanasan sementara mendapatkan tertinggi.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

ساخت نانو بلورک‌های δ-7O3Cu2YBa به روش مکانوشیمیایی و بررسی دمای گذار ترکیبات -7O3Cu2YBa(x-1) + 2 xMnO (02/0 ،015/0 ،01/0 ،005/0 ،0 = x)

In this research, YBa2Cu3O7-d (0 < d < 1) nanocrystalite superconductor was prepared by mechanochemical alloying method. We synthesized YBa2Cu3O7-d via mixing the BaCO3, Y2O3, CuO powders and milling in SPEX 8000 for 5h with weight ratio of ball to powder 10:1 and steel balls of 11mm diameter, followed by heating for 4h at 850 ˚C. The superconductor phase formation process was completed with si...

متن کامل

بررسی‌های ساختاری و مغناطیسی نانوذرات‌ پروسکایت LaMn1-xCoxO3 (0/1، 75/0، 5/0، 25/0، 0/0 = x)

In this work, the structural and magnetic properties of LaMn1-xCoxO3 (x = 0.00, 0.25, 0.50, 0.75, 1.00) are investigated. The structural characterization of compounds by X-ray powder diffraction is evidence for a rhombohedral structure (R -3c space group). Much less increase of the unit cell volume suggests that Co enters in lattice as Co+2 for x ≤ 0.5 while much more decrease of the unit cell ...

متن کامل

اثر جانشانی Mn2+ بر خواص ساختاری و مغناطیسی نانوفریت‌های Ni(0.5-x)MnxZn0.5Fe2O4 (5/0 ،35/0 ،25/0 ،0 = x) تهیه‌شده به روش هم‌رسوبی

Nanoparticles of  Ni(0.5-x)MnxZn0.5Fe2O4 with stoichiometric proportion, x = 0, 0.25, 0.35, 0.5, were prepared via the chemical co-precipitation process. The structure properties of nanoparticles were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Their magnetic properties were evaluated on a vibrating sample magnetometer ...

متن کامل

Scalar mesons and δ 0 − δ 2 at KLOE

The KLOE measurements of φ radiative decays and of the ratio Γ(K S → π + π − (γ))/Γ(K S → π 0 π 0) are discussed. The first measurement aims at understanding the real nature of the scalar mesons a 0 and f 0 , whose possible compositions are q ¯ q, qq ¯ q ¯ q, or K ¯ K molecule. The second measurement is related to the estimate of the phase shift difference δ 0 − δ 2. Previous measurements were ...

متن کامل

مطالعه خواص مغناطیسی و الکتریکی نانو فریت های 4o2fe x cu (x- 5/0)mn 5/0 ni (5/0 ، 3/0 ،1/0 ، 0/0=x )

نانوذرات مغناطیسی فریت نیکل- منگنز- مس عمدتأ در دارورسانی مغناطیسی، محیط های مغناطیسی ضبط داده ها، حسگرهای گازی، مدارهای فرکانس بالا و ذخیره اطلاعات و ... کاربرد فراوانی دارند. در این پایان نامه نانوذرات مغناطیسی فریت نیکل - منگنز - مس با درصدهای متفاوت جانشانی مس به جای منگنز به روش هم رسوبی شیمیایی تهیه شدند و خواص ساختاری، مغناطیسی و الکتریکی آنها مورد مطالعه و بررسی قرارگرفت. برای مشخصه یاب...

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Sains Malaysiana

سال: 2021

ISSN: ['0126-6039', '2735-0118']

DOI: https://doi.org/10.17576/jsm-2021-5006-23