Parametric studies of failure mechanisms in elastic EB-PVD thermal barrier coatings using FEM
نویسندگان
چکیده
منابع مشابه
Residual Stresses of Eb-pvd Thermal Barrier Coatings Exposed to High Temperature
The substrate material was nickel-based superalloy (In738LC), and CoNiCrAlY was pressureless plasma-sprayed on the substrate as the bond coating. As the top coating, zirconia with 4 mol% yttria was electron beam-physical vapor deposited (EB-PVD) on the rotating substrate. The rotation speeds in the EB-PVD process were 5, 10 and 20rpm. The specimens were exposed to 1273K in air atmosphere for 20...
متن کاملErosion, Corrosion and Erosion-Corrosion of EB PVD Thermal Barrier Coatings
Electron beam (EB) physical vapour deposited (PVD) thermal barrier coatings (TBCs) have been used in gas turbine engines for a number of years. The primary mode of failure is attributed to oxidation of the bondcoat and growth of the thermally grown oxide (TGO), the alumina scale that forms on the bondcoat and to which the ceramic top coat adheres. Once the TGO reaches a critical thickness the T...
متن کاملFailure Mechanisms Investigation in Thermal Barrier Coatings under Isothermal and Non-sothermal Fatigue Loadings using Design of Experiments
In this article, failure and fracture mechanisms in an aluminum alloy (which has been used in diesel internal combustion engines), with and without ceramic thermal barrier coatings, have been investigated under isothermal and non-isothermal fatigue loadings. In this research, the base material is an aluminum-silicon-magnesium alloy and the thermal barrier coating includes a metallic bond coat l...
متن کاملfailure mechanisms investigation in thermal barrier coatings under isothermal and non-sothermal fatigue loadings using design of experiments
in this article, failure and fracture mechanisms in an aluminum alloy (which has been used in diesel internal combustion engines), with and without ceramic thermal barrier coatings, have been investigated under isothermal and non-isothermal fatigue loadings. in this research, the base material is an aluminum-silicon-magnesium alloy and the thermal barrier coating includes a metallic bond coat l...
متن کاملNanostructural studies of PVD TiAlB coatings
TiAlB coatings with different compositions were deposited by co-sputtering from TiAl and TiB2 targets onto AISI316 stainless steel substrates at a temperature of 170(C. The stoichiometry and nanostructure have been studied by x-ray photoelectron spectroscopy (XPS), x-ray diffraction (XRD) and transmission electron microscopy (TEM). Analysis of the XPS spectra suggests the presence of phases in ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Solids and Structures
سال: 2006
ISSN: 0020-7683
DOI: 10.1016/j.ijsolstr.2005.07.037