Oxidative Dehydrogenation of Propane over Nanostructured Mesoporous VOx/CexZr1-xO2 Catalysts

نویسندگان

چکیده

High-surface-area mesoporous CexZr1-xO2 materials synthesized through a surfactant-assisted approach of nanocrystalline particle assembly are utilized as promising support for VOx-based catalysts. The catalytic properties the resultant VOx/CexZr1-xO2 nanocatalysts evaluated by oxidative dehydrogenation propane using microreactor-GC system. It is indicated that catalyst particles on nanoscale, having structure with uniform pore-size distribution and high surface area. behavior these nanostructured VOx/CexZr1-xO2 catalysts propane reaction relies vanadia loading amount, calcination temperature, area and Ce/Zr ratio supports, the size active compounds, additional contribution to propylene formation derives from propane under oxygen-lean conditions. catalyst prepared 8 wt% vanadia loading Ce0.2Zr0.8O2 exhibits high stable performance in propane reaction.&nbsp

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Catalytic oxidative dehydrogenation of propane over Mg–V/Mo oxides

Fifteen distinct MgO–V2O5, MgO–MoO3, MgO–V2O5–MoO3, and V2O5–MoO3 compositions were prepared using sol–gel chemistry and their selectivities and conversions for propane oxidative dehydrogenation (ODH) to propylene were measured. The vanadates were more active than the molybdates at lower temperatures; however, the molybdates exhibited higher selectivities at similar conversions. An increase in ...

متن کامل

Physicochemical Properties and Catalytic Performances of Nanostructured V2O5 over TiO2 and γ-Al2O3 for Oxidative Dehydrogenation of Propane

Propylene is an important raw material and extensively used in the petrochemical industry. There has been a continuously growing demand for propylene in recent years around the world1–3. The majority of propylene is produced as a byproduct from processes such as steam cracking of naphtha and fluid catalytic cracking (FCC)4,5. Additional sources of propylene included dehydrogenation of propane, ...

متن کامل

Catalytic Properties of Supported MoO3 Catalysts for Oxidative Dehydrogenation of Propane

The effects of MoOx structure on propane oxidative dehydrogenation (ODH) rates and selectivity were examined on Al2O3-supported MoOx catalysts with a wide range of surface density (0.4-12 Mo/nm), and compared with those obtained on MoOx/ZrO2. On MoOx/Al2O3 catalysts, propane turnover rate increased with increasing Mo surface density and reached a maximum value for samples with ~ 4.5 Mo/nm. All ...

متن کامل

Synthesis of Three-Dimensionally Ordered Macroporous NiCe Catalysts for Oxidative Dehydrogenation of Propane to Propene

Three-dimensionally ordered macroporous (3DOM) NiCe catalysts with different Ni/Ce molar ratio were fabricated using the colloidal crystal templating method. The physic-chemical properties of the samples were characterized by various techniques, including N2 adsorption–desorption, X-ray diffraction (XRD), transmission electron microscopy (TEM), Raman, and H2-temperature-programmed reduction (TP...

متن کامل

Metal–Organic Framework Supported Cobalt Catalysts for the Oxidative Dehydrogenation of Propane at Low Temperature

Zr-based metal-organic frameworks (MOFs) have been shown to be excellent catalyst supports in heterogeneous catalysis due to their exceptional stability. Additionally, their crystalline nature affords the opportunity for molecular level characterization of both the support and the catalytically active site, facilitating mechanistic investigations of the catalytic process. We describe herein the...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Advanced Materials Science and Technology

سال: 2022

ISSN: ['2717-526X']

DOI: https://doi.org/10.37155/2717-526x-0402-5