Oxidation Resistance and Residual Strength of Laminated ZrB2-SiC-G Ceramics at 1300℃
نویسندگان
چکیده
منابع مشابه
Oxidation of ZrB2-SiC Composites at 1600 °C: Effect of Carbides, Borides, Silicides, and Chopped Carbon Fiber
The aim of this work is to optimize the oxidation resistance of ZrB2-SiC-based composites with different additives. Effect of nine factors including SiC, Cf, MoSi2, HfB2 and ZrC contents, milling time of Cf (M.t) and SPS parameters such as temperature, time and pressure on oxidation resistance in four levels was investigated. Taguchi design was applied to explore effective parameters for ...
متن کاملMicrostructure and high-temperature strength of textured and non-textured ZrB2 ceramics
Zirconium diboride (ZrB2) ceramic possesses a unique combination of nice mechanical performance, high melting point (> 3000 °C) and great high-temperature oxidation resistance (up to 1600 °C), which makes it a promising material system for ever-increasing ultra-high temperature (UHT) applications. However, ZrB2 suffers from poor mechanical performance at UHTs, which could strongly limit its app...
متن کاملFabrication and inspection of C/Cf-ZrB2-ZrC-SiC and C/Cf-ZrB2-SiC composite parts resistant to ablation by pressureless sintering method
In this research, the aim is to achieve strong and ablation-resistant composite parts C / Cf-ZrB2-ZrC-SiC and C / Cf-ZrB2-SiC by non-pressure sintering method. C / Cf-ZrB2-SiC samples were prepared using synthesized ZrB2 and SiC powders between layers of resin-impregnated carbon fabric. After pressing with pressure 5 times at 1600 وC and heat treatment for 2 hours in a controlled atmosphere fur...
متن کاملreview of the mechanical and thermal properties of high temperature Diboride ceramics
Ceramic borides, carbides and nitrides with high melting point, relatively good resistance to oxidation and corrosive environments are considered by many researchers in various high temperature industries, which is known from the family of materials as high temperature ceramic (UHTC). To be. All UHTCs have very strong bonds that give them structural stability at high temperatures, and among the...
متن کاملFracture and Deformation
The high-velocity impact resistance of hot-pressed zirconum diboride with 30 volume percent silicon carbide was studied using a combined experimental and computational approach. Test specimens in the form of 2 mm thick polished disks were impacted with -0.8 mm diameter tungsten carbide spheres at velocities up to 320 d s . The intrinsic flexure strength of the specimens was -1000 MPa. The flexu...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Inorganic Materials
سال: 2017
ISSN: 1000-324X
DOI: 10.15541/jim20160638