Oxidation Behavior of Heat Resisting Steels under Cyclic Heating
نویسندگان
چکیده
منابع مشابه
THE OXIDATION RESISTANCE OF HIGH ALUMINUM HEAT RESISTANT STEELS
Abstract: In this research, the oxidation behaviour of high Aluminum heat resistant steel (%25Cr,%20Ni,%8Al) hasbeen evaluated at the temperature range of (1000-1300ºC).The results showed that there was no countinous healinglayer on the surface of the alloy when Al increased up to %5.5 and the oxidation resistance of steel decreased due toformation of spinel oxides on the surface.By increasing ...
متن کاملCyclic oxidation behavior of uncoated and aluminum-rich nickel aluminide coated Rene-80 superalloy
In this study, aluminide coating was employed to enhance the high-temperature cyclic oxidation of Rene-80 superalloy at 950ºC. The microstructural aspects and phase constituents of samples were investigated with scanning electron microscopy (SEM) and x-ray diffraction (XRD) techniques. The result of oxidation tests showed that the weight gain in the uncoated sample was considerably higher than...
متن کاملSubstructure Model for Concrete Behavior Simulation under Cyclic Multiaxial Loading
This paper proposes a framework for the constitutive model based on the semi-micromechanical aspects of plasticity, including damage progress for simulating behavior of concrete under multiaxial loading. This model is aimed to be used in plastic and fracture analysis of both regular and reinforced concrete structures, for the framework of sample plane crack approach. This model uses multilamina...
متن کاملIsothermal and cyclic oxidation behavior of AISI 430 ferritic stainless steel coated with titanium
In order to improve the oxidation resistance of ferritic stainless steel, it is possible to deposit a protective coating on steel substrate. In this research through the usage of pack cementation method a coating of titanium was applied on the surface of AISI 430 stainless steel. Scanning Electron-Microscopy (SEM), Energy- Dispersive X-ray spectrometry (EDAX) and X-ray diffraction (XRD) were us...
متن کاملHigh Temperature Behavior of Dual Phase Steels
Dual phase steels with different martensite volume fraction and morphology were tensile tested at a temperature range of 25 to 5500C. Stress-strain curves of all steels showed serration flow at temperatures of 250 and 3500C, and smooth flow at the other temperatures. Both yield and ultimate tensile strengths increased with increasing testing temperature up to about 450<sup...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 1977
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane1955.63.5_681