Over–current carrying characteristics of rectangular–shaped YBCO thin films prepared by MOD method
نویسندگان
چکیده
منابع مشابه
Photodegradation of reactive red 222 using TiO2 nanostructured thin films prepared by modified sol-gel method
In this paper, a modified sol-gel method using peroxotitanic acid sol (PTA) was applied for the preparation of TiO2 nanostructured thin films on glass plates. The peroxotitanic acid sol was synthesized using titanium isopropoxide, isopropylalchol, H2O and hydrogen peroxide. TiO2 films were then calcined at 500oC and characterized by X-ray diffraction ...
متن کاملPhotodegradation of reactive red 222 using TiO2 nanostructured thin films prepared by modified sol-gel method
In this paper, a modified sol-gel method using peroxotitanic acid sol (PTA) was applied for the preparation of TiO2 nanostructured thin films on glass plates. The peroxotitanic acid sol was synthesized using titanium isopropoxide, isopropylalchol, H2O and hydrogen peroxide. TiO2 films were then calcined at 500oC and characterized by X-ray diffraction ...
متن کاملStructural characterization of epitaxial YBCO thin films prepared by a fluorine-free sol–gel method for coated conductors
Using a fluorine-free sol–gel method, both cand a-axis textured YBCO thin films were synthesized in low oxygen partial pressure. The experimental results of both x-ray diffraction 2θ scan and pole figure showed well epitaxial grown films on LaAlO3 (LAO) single crystal substrates. When the processing condition was altered, the scanning electron microscopy indicated a large fraction of a-axis ori...
متن کاملStructural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films
Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...
متن کاملStructural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films
Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Physics: Conference Series
سال: 2008
ISSN: 1742-6596
DOI: 10.1088/1742-6596/97/1/012236