Origin of compression-induced failure in brittle solids under shock loading
نویسندگان
چکیده
منابع مشابه
Loading rates and the dynamic initiation toughness in brittle solids
The experimentally determined marked rise of the stress intensity factor required to initiate crack propagation in brittle solids under variably high loading rates, is analyzed. This problem of fracture initiation at the tip of a crack is considered in terms of activating a flaw at some distance away from the tip. By using a semi-infinite crack in an unbounded two-dimensional solid subjected to...
متن کاملSpall strength of a zirconium-based bulk metallic glass under shock-induced compression-and-shear loading
We present results of a series of plate-impact experiments conducted to understand spall threshold in a zirconium-based bulk metallic glass (BMG), Zr41.25Ti13.75Ni10Cu12.5Be22.5, following normal shock-induced compression and combined compression-and-shear loading. The experiments were conducted using a 82.5 mm bore single-stage gas-gun. A multibeam VALYN VISAR was used to measure the particle–...
متن کاملExperimental Investigation of Thermally Induced Interacting Cracks in Brittle Solids
AbstracbThe results of an experimental investigation of thermally induced parallel edge cracks in a half-plane consisting of brittle material are reported. A free edge of a glass plate heated to a uniform temperature, was brought in contact with a liquid bath cooled by dry ice. The thermal contraction of the boundary layer produced interacting tension cracks. When no initial cracks existed, a l...
متن کاملA failure criterion for brittle elastic materials under mixed-mode loading
The failure criterion of Leguillon at reentrant corners in brittle elastic materials (Leguillon 2002, Eur J Mech A/Solids 21: 61–72; Leguillon et al. (2003), Eur J Mech A—Solids 22(4): 509–524) validated in (Yosibash et al. 2004, Int J Fract 125(3–4): 307–333) for mode I loading is being extended to mixed mode loading and is being validated by experimental observations. We present an explicit d...
متن کاملCumulative Fatigue Damage Under stepwise Tension-Compression Loading
Rock structures are subjected to cyclic tension-compression loading due to a blasting, earthquake, traffic and injection-production in underground storage case. Therefore study the fatigue behavior of rock samples under this type of loading is required. In this study, the accumulated fatigue damage for a Green Onyx rock sample which consisted of only one mineral composition with two-step high-l...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Physical Review B
سال: 2015
ISSN: 1098-0121,1550-235X
DOI: 10.1103/physrevb.92.144101