Orientation Dependence of Work Hardening of Cu-10 at%Al Alloy Single Crystals near the [111] Axis
نویسندگان
چکیده
منابع مشابه
THE INFLUENCE OF DRY SLIDING ON PRCIPITATION HARDENING BEHAVIORS OF Al-Cu-Si ALLOY
Abstract: Cold working performed before an aging treatment has a significant effect on size and amount of precipitate produced. This could be caused by the increase in defect density, such as vacancies and dislocations. In this research, the Al-Cu-Si alloy was solution-treated, wear-tested and then artificially aged for a period of 1–5 h. Changes in the amount of precipitate, in the lattice par...
متن کاملExperimental Study on the Magnetomechanical Characteristics of Ni-Mn-Ga Ferromagnetic Shape Memory Alloy Single Crystals
Magnetic shape memory properties of Ni-Mn-Ga single crystals were characterized by measurement of stress-induced martensite reorientation under constant magnetic fields. Also magnetic field-induced strain as a function of the applied magnetic field under different constant compressive stress levels has been investigated. All the experiments were performed at room temperature in which the sample...
متن کاملOrientation dependence of the anomalous Hall resistivity in single crystals of Yb14MnSb11
The Hall resistivity, electrical resistivity, and magnetization of single crystals of the tetragonal ferromagnet Yb14MnSb11 are reported as a function of the direction of the current I and magnetic field H with respect to the principal crystallographic axes. With I along the unique c direction and H in the a-b plane, the anomalous Hall resistivity in the limit of zero applied field is negative ...
متن کاملStrain hardening behavior of aluminum alloyed Hadfield steel single crystals
Very high strain hardening coefficients (=G/23) are observed for aluminum-alloyed face-centered cubic Hadfield steel single crystals under tensile loading. Alloying with aluminum suppressed deformation twinning in two of the three crystallographic orientations studied, and transmission electron microscopy results revealed the existence of dense dislocation walls (sheets) along crystallographic ...
متن کاملLow-temperature orientation dependence of step stiffness on {111} surfaces
For hexagonal nets, descriptive of 111 fcc surfaces, we derive from combinatoric arguments a simple, low-temperature formula for the orientation dependence of the surface step line tension and stiffness, as well as the leading correction, based on the Ising model with nearest-neighbor NN interactions. Our formula agrees well with experimental data for both Ag and Cu 111 surfaces, indicating tha...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of the Japan Institute of Metals
سال: 1976
ISSN: 0021-4434,2432-4701
DOI: 10.2320/matertrans1960.17.837