Ordered mesoporous carbons with body centred cubic pore structure
نویسندگان
چکیده
منابع مشابه
Characterization of the pore structure of three-dimensionally ordered mesoporous carbons using high resolution gas sorption.
The use of colloidal crystals with various primary particle sizes as templates leads to the formation of three-dimensionally ordered mesoporous (3DOm) carbons containing spherical pores with tailorable pore size and extremely high pore volumes. We present a comprehensive structural characterization of these novel carbons by using nitrogen (77.4 K) and argon (87.3 K) adsorption coupled with the ...
متن کاملTemplate Synthesis of Three-Dimensional Cubic Ordered Mesoporous Carbon With Tunable Pore Sizes
Three-dimensional cubic ordered mesoporous carbons with tunable pore sizes have been synthesized by using cubic Ia3d mesoporous KIT-6 silica as the hard template and boric acid as the pore expanding agent. The prepared ordered mesoporous carbons were characterized by powder X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and nitrogen adsorption-desorption anal...
متن کاملTuning the Pore Geometry of Ordered Mesoporous Carbons for Enhanced Adsorption of Bisphenol-A
Mesoporous carbons were synthesized via both soft and hard template methods and compared to a commercial powder activated carbon (PAC) for the adsorption ability of bisphenol-A (BPA) from an aqueous solution. The commercial PAC had a BET-surface of 1027 m²/g with fine pores of 3 nm and less. The hard templated carbon (CMK-3) material had an even higher BET-surface of 1420 m²/g with an average p...
متن کاملSynthesis of ordered mesoporous carbons with channel structure from an organic-organic nanocomposite.
Mesoporous carbons with ordered channel structure (COU-1) have been successfully fabricated via a direct carbonization of an organic-organic nanocomposite.
متن کاملHighly ordered cubic mesoporous electrospun SiO2 nanofibers.
Cubic (Im3[combining macron]m) mesoporous silica nanofibers were successfully prepared using a new F127-PVA-SiO2 tri-constituent assembly approach by the electrospinning technique. PVA was used to protect the F127 directed cubic micelles which usually deform during electrospinning. The preformed Au NPs can be loaded inside the mesopores of the nanofibers.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Carbon Trends
سال: 2021
ISSN: 2667-0569
DOI: 10.1016/j.cartre.2021.100051