Order-disorder morphologies in rapidly solidified ε/ε′-Ni5Ge3 intermetallic
نویسندگان
چکیده
منابع مشابه
TEM INVESTIGATION OF RAPIDLY SOLIDIFIED NDFEB HARD MAGNETIC MATERIAL
The surface condition and microstructure of near stoichiometric (Fe823Ndll.8B5.9) Nd-Fe-B alloy ribbons and the effect of melt spinning parameters were investigated using optical, scanning and transmission electron microscopes (SEM, TEM). The formation of gas pockets on the roll surface of the ribbons during melt spinning can prevent heat transform and result in local coarse grains. The local t...
متن کاملRapidly Solidified Magnetic Nanowires and Submicron Wires
Magnetically soft amorphous glass-coated microwires are suitable for numerous sensor applications. Their typical dimensions – metallic nucleus diameter of 1 to 50 m and glass coating thickness of 1 to 30 m – make them promising candidates for high frequency applications, especially given their sensitive giant magneto-impedance (GMI) response in the MHz and GHz ranges (Torrejón et al, 2009). T...
متن کاملRadiation Interactions With Cerrobend Metal Rapidly Solidified From Melt
Mustafa Kamal, Abu-Bakr El-BediwiTamer Dawod* and Adel. S. Waqlan** Metal Physics Lab. Physics Department, Faculty of Science –Mansoura University, Egypt. * Medical Physics Unit, Clinical Oncology and Nuclear Medicine Dept., Faculty of Medicine, Mansoura University **On leave, M.sc student, Ministry of Higher Education, Yemen. [email protected], [email protected] [email protected]...
متن کاملGlassy and icosahedral phases in rapidly solidified Ti–Zr–Hf–(Fe, Co or Ni) alloys
The icosahedral quasicrystalline, amorphous plus crystalline and glassy phases were formed in Ti40Zr20Hf20(3d-LTM)20 alloys (3d-LTM=3d late transition metals Fe, Co and Ni). The icosahedral phase formed in the melt-spun Ti40Zr20Hf20Fe20 alloy is metastable and the average size of the quasicrystalline icosahedral particles precipitated in the amorphous matrix is 5 nm. The metastable icosahedral ...
متن کاملMagnetism-Structure Correlations during the ε→τ Transformation in Rapidly-Solidified MnAl Nanostructured Alloys
Magnetic and structural aspects of the annealing-induced transformation of rapidly-solidified Mn55Al45 ribbons from the as-quenched metastable antiferromagnetic (AF) ε-phase to the target ferromagnetic (FM) L10 τ-phase are investigated. The as-solidified material exhibits a majority hexagonal ε-MnAl phase revealing a large exchange bias shift below a magnetic blocking temperature TB~95 K (Hex~1...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Alloys and Compounds
سال: 2018
ISSN: 0925-8388
DOI: 10.1016/j.jallcom.2017.12.253