Optimisation of the high velocity oxygen fuel (HVOF) parameters to produce effective corrosion control coatings on AZ91 magnesium alloy
نویسندگان
چکیده
منابع مشابه
Possibilities of Utilization High Velocity Oxygen Fuel (hvof) Coatings in Conditions of Thermal Cyclic Loading
The item deals with the possibilities of utilization HVOF coatings in thermal cyclic loading conditions. There were evaluated three types of coatings based on WC-Co, WC-Co-Cr and Cr3C2-25NiCr. The quality of coatings was evaluated in terms of their adhesion as sprayed and also during the cyclic thermal loading, EDX analysis and evaluation of microhardness. Construction and structure of coatings...
متن کاملApplication of High-Velocity Oxygen-Fuel (HVOF) Spraying to the Fabrication of Yb-Silicate Environmental Barrier Coatings
From the literature, it is known that due to their glass formation tendency, it is not possible to deposit fully-crystalline silicate coatings when the conventional atmospheric plasma spraying (APS) process is employed. In APS, rapid quenching of the sprayed material on the substrate facilitates the amorphous deposit formation, which shrinks when exposed to heat and forms pores and/or cracks. T...
متن کاملEffect of Ti on the Mechanical Properties and Corrosion of Cast AZ91 Magnesium Alloy
Ti addition to AZ91 alloy was been investigated with conventional casting. The microstructure and mechanical property were examined. The Corrosion resistance of all the different Ti addition content alloy was studied in 3.5% NaCl solution through weight loss measurement in constant immersion conditions and potentiodynamic polarization experiments. The results show that addition of Ti with an am...
متن کاملThe Effect of Environmental Parameters on the Corrosion Behavior of Simple Shear Extruded AZ91 Magnesium Alloys
In this study, the effects of forming method (extrusion) and environmental factors (solution pH and temperature) on the corrosion performance of AZ91 magnesium alloys were investigated using potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM) and salt spray techniques. The polarization test results of the specimens showed that simple sh...
متن کاملHigh Temperature Corrosion Behavior of HVOF, Fe3Al Coatings
This work evaluates the suitability of iron aluminide coatings for use in high temperature fossil fuel combustion environments, such as boiler applications. The coatings are applied using High Velocity Oxy-Fuel (HVOF) thermal spray techniques. Bulk Fe3Al coatings are known to exhibit excellent oxidation and sulfidation resistance at high temperatures, however, the behavior of HVOF-deposited Fe3...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials and Corrosion
سال: 2014
ISSN: 0947-5117
DOI: 10.1002/maco.201407982