Optical properties of Er3+ doped alkali chlorophosphate glasses for optical amplifiers
نویسندگان
چکیده
منابع مشابه
Optical and Thermal Properties of Mixed Alkali Phosphate Based Glasses
Glassy samples with a composition of 40P2O5–30V2O5–(30-x)Li2O– xK2O, 0<x<30 (mol %) were prepared by the conventional melt quenching technique in two forms of bulk and blown film. X-ray diffraction patterns corroborated the amorphous feature of the samples. Density of samples was investigated by using Archimedes principle. Based on absorption and reflection spectra, indirect a...
متن کاملStructural Investigation, Physical and Optical Properties of Mixed Alkali Bismuth Borate Glasses
Lead free, eco-friendly bismuth borate glasses doped with alkali oxides of composition xLi2O+(30-x)Na2O+55B2O3+15Bi2O3 (x = 5,10,15,20,25) were prepared by melt quenching technique. Amorphous nature of glasses was confirmed by X-ray diffraction. Density measurements were carried out at room temperature by standard principle of Archimedes with Xylene as an immersion liquid. The non-linear ...
متن کاملcontrol of the optical properties of nanoparticles by laser fields
در این پایان نامه، درهمتنیدگی بین یک سیستم نقطه کوانتومی دوگانه(مولکول نقطه کوانتومی) و میدان مورد مطالعه قرار گرفته است. از آنتروپی ون نیومن به عنوان ابزاری برای بررسی درهمتنیدگی بین اتم و میدان استفاده شده و تاثیر پارامترهای مختلف، نظیر تونل زنی(که توسط تغییر ولتاژ ایجاد می شود)، شدت میدان و نسبت دو گسیل خودبخودی بر رفتار درجه درهمتنیدگی سیستم بررسی شده اشت.با تغییر هر یک از این پارامترها، در...
15 صفحه اولOptical properties of Nd doped Bi2O3-PbO-Ga2O3 glasses.
The optical properties of a new family of neodymium doped BPG (Bi2O3-PbO-Ga2O3 ) glasses are presented. We measured a high refractive index, of 2.5, and a transmission cutoff in the far infrared at 8microm. Three intense emission bands are observed centered at 877nm, 1066nm and 1341nm. The emission cross-section is 10 -20 cm 2 and the total spectral linewidth is 30nm at 1066nm. The Judd-Ofelt p...
متن کاملSpectroscopic properties and upconversion mechanisms in Er3+-doped fluoroindate glasses.
Fluorindate glasses containing 1,2,3,4 ErF3 mol % were prepared in a dry box under argon atmosphere. Absorption, Stokes luminescence ~under visible and infrared excitation!, the dependence of S3/2, I11/2, and I13/2 lifetimes with Er concentration, and upconversion under Ti-saphire laser excitation at l5790 nm were measured, mostly at T577 and 300 K. The upconversion results in a strong green em...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Optical Materials
سال: 2008
ISSN: 0925-3467
DOI: 10.1016/j.optmat.2008.02.007