On the Magnetic Properties of Quench-Hardened Magnet Steel
نویسندگان
چکیده
منابع مشابه
control of the optical properties of nanoparticles by laser fields
در این پایان نامه، درهمتنیدگی بین یک سیستم نقطه کوانتومی دوگانه(مولکول نقطه کوانتومی) و میدان مورد مطالعه قرار گرفته است. از آنتروپی ون نیومن به عنوان ابزاری برای بررسی درهمتنیدگی بین اتم و میدان استفاده شده و تاثیر پارامترهای مختلف، نظیر تونل زنی(که توسط تغییر ولتاژ ایجاد می شود)، شدت میدان و نسبت دو گسیل خودبخودی بر رفتار درجه درهمتنیدگی سیستم بررسی شده اشت.با تغییر هر یک از این پارامترها، در...
15 صفحه اولFinite Element Analysis of Hardened Steel Cutting
Hard machining, as attractive replacement for many rough and finish grinding operation, generates high cutting forces and temperature that enhance tool wear when act together. Therefore, the tool geometry and machining parameters have to be carefully optimized for a given material. Because of high cost and time consuming experimental work up-to-date advanced software for modeling and simulation...
متن کاملMagnetic Properties and Structure of Cobalt Hardened Gold
The iq-hmziitation of an experimental design to investigate the variation in cobalt hardened gold electrodeposition produced a series of electrodeposited AuCo alloys which had been stripped from their copper substrates. The magnetic properties of these electroplatings were measured at room temperature using the Faraday method. These measurements showed the presence of two magnetic phases. One p...
متن کاملOn machining of hardened AISI D2 steel with PCBN tools
This paper describes an experimental investigation on machining of a difficult-to-cut material, AISI D2 steel of hardness 62 HRC with PCBN tools. It was found that the most feasible feeds and speeds fall in the ranges 0.08–0.20 mm/rev and 70–120 m/min, respectively and that most of the tested PCBN tools reached the end of life mainly due to flank wear. The highest acceptable values of tool life...
متن کاملCopper Precipitation Hardened, High Strength, Weldable Steel
Steel containing 0.03% carbon, 1.35% copper and 0.84% nickel had yield strength in the 540-625 MPa (78-90 Ksi) range depending on thickness, ultimate tensile strength in the 625-690 MPa (90100 Ksi) range, and 25-30% elongation when air cooled after hot rolling. No brittle heat-affected zone was formed during manual or automatic submerged arc welding without pre-heating or postheating. The fract...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1958
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.22.2_63