On the Fillet Weld Cracking of 50kg/mm2 Grade High Strength Steels
نویسندگان
چکیده
منابع مشابه
Effect of Acicular Ferrite on Cracking Sensibility in the Weld Metal of Q690+Q550 High Strength Steels
High strength steels Q690+Q550 were welded using three different welding wires without preheating by gas shielded arc welding process. Microstructural characteristics of weld metals and nucleation mechanism of acicular ferrite were investigated by means of scanning electron microscope (SEM), energy dispersive spectrum (EDS) and transmission electron microscope (TEM). The straight Y-groove test ...
متن کاملHigh-Strength Bainitic Steels
With careful design, mixed microstructures consisting of fine plates of upper bainitic ferrite separated by thin films of stable retained austenite have exhibited impressive combinations of strength and toughness in highsilicon bainitic steels. The silicon suppresses the precipitation of brittle cementite leading to an improvement in toughness. The essential principles governing the optimisatio...
متن کاملthe effect of taftan pozzolan on the compressive strength of concrete in the environmental conditions of oman sea (chabahar port)
cement is an essential ingredient in the concrete buildings. for production of cement considerable amount of fossil fuel and electrical energy is consumed. on the other hand for generating one tone of portland cement, nearly one ton of carbon dioxide is released. it shows that 7 percent of the total released carbon dioxide in the world relates to the cement industry. considering ecological issu...
A Comparison of Hydrogen Embrittlement and Stress Corrosion Cracking in High Strength Steels
The purpose of this study was to compare the known behavior of hydrogen embrittled high-strength steel to the characteristics of environmentallyinduced stress corrosion failure where hydrogen is continuously generated at the specimen surface. The incubation time for the initiation of slow crack growth was accelerated by prestressing for a fixed time below the lower critical limit. These results...
متن کاملCharacteristics of Hydrogen Embrittlement, Stress Corrosion Cracking and Tempered Martensite Embrittlement in High-strength Steels
Characteristics of tempered martensite embrittlement (TME), hydrogen embrittlement (HE), and stress corrosion cracking (SCC) in high-strength steels are reviewed. Often, it is important to determine unambiguously by which of these mechanisms failure occurred, in order to suggest the right actions to prevent failure recurrence. To this aim, samples made of high-strength AISI 4340 alloy steel wer...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Welding Society
سال: 1970
ISSN: 0021-4787,1883-7204
DOI: 10.2207/qjjws1943.39.3_156