On recrystallization of Al-Ag and Al-Cu alloys
نویسندگان
چکیده
منابع مشابه
INFLUENCE OF THE Al CONTENT ON THE PHASE TRANSFORMATIONS IN Cu-Al-Ag ALLOYS
The literature about alloys of the Cu-Al system is extensive, due to its practical use. These alloys are of low cost and present good strength and hardness, depending on the Al content. They are used for making sleeves, guides, seats, flanges, gear wheels and many other critical small parts, as electrolysis cell cathodes, circuit plates and casting moulds when high thermal conductivity is neede...
متن کاملElemental separation in nanocrystalline Cu-Al alloys
Y. B. Wang, X. Z. Liao, Y. H. Zhao, J. C. Cooley, Z. Horita, and Y. T. Zhu School of Aerospace, Mechanical and Mechatronic Engineering, The University of Sydney, Sydney, NSW 2006, Australia School of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094, China Division of Materials Science and Technology, Los Alamos National Laboratory, Los Alamos, New ...
متن کاملClustering and Segregation of Mg and Ag Atoms during the Precipitation Processes in Al(-Li)-Cu-Mg-Ag Alloys
This paper reports three dimensional atom probe (3DAP) results of solute clusters and precipitates in early aging stages of Al-Cu(-Li) alloys containing small amounts of Ag and Mg atoms. In an as-quenched Al-1.9Cu-0.3Mg-0.2Ag (at.%) alloy, solute atoms are uniformly dissolved. On aging for 5 s at 180°C, Ag and Mg atoms form co-clusters. These co-clusters do not have well defined shape, but they...
متن کاملTENSILE TESTING OF FREE-STANDING Cu, Ag AND Al THIN FILMS AND Ag/Cu MULTILAYERS
ÐFree standing polycrystalline thin ®lms with a strong h111i texture were tested in uniaxial tension. Studied were electron-beam deposited Ag, Cu and Al ®lms, and Ag/Cu multilayers consisting of alternating Ag and Cu layers of equal thickness, between 1.5 nm and 1.5 mm (bilayer repeat length, l, between 3 nm and 3 mm). The ®lms had a total thickness of about 3 mm. A thin polymeric two-dimension...
متن کاملMICROSTRUCURE AND STRENGTHENING OF Al-Li-Cu-Mg ALLOYS
A detailed quantitative model for the strengthening of monolithic alloys and composites due to precipitation strengthening, solution strengthening, grain and subgrain strengthening, strengthening by dislocations and load transfer to ceramic inclusions is presented. The model includes a newly derived description of the effect of a precipitate free zone (PFZ) around the reinforcing phase incorpor...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Japan Institute of Light Metals
سال: 1958
ISSN: 0451-5994
DOI: 10.2464/jilm.8.5_18