On Rapid Heat Patenting of High Carbon Steel Wire Rods

نویسندگان
چکیده

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Static Strain Aging Behavior of Low Carbon Steel Drawn Wire

The static strain aging is a phenomenon that can change the mechanical properties of low carbon steels. Thus, the static strain aging behavior of low carbon steel wires after drawing process is studied. To do so, the wires are austenitized at different temperatures and cooled in different rates. Then the wires are drawn and aged at a specific temperature and time. Before and after aging of each...

متن کامل

Developing Very Fine Nanopearlitic Structure in a High Carbon Steel Wire before Drawing

The effects of steel wire patenting process parameters on very fine interlamellar spacing in the pearlitic steel wire were investigated and the optimized condition of the process was achieved. In this work, the initial nanopearlitic structure was obtained in a 0.72 wt% carbon steel wire before the wire drawing process. The results were the minimum interlamellar spacing of 35 nm and maximum ulti...

متن کامل

The Effect of Multiple Bending of Wire on the Residual Stresses of High Carbon Steel Wires

R. Kruzel, M. Suliga, Czestochowa University of Technology, Czestochowa, Poland Steel tire cord, springs and rope wires belong to the group of metal products from which the low residual stresses are required. In this paper the eff ect of multiple bending of wire on residual stresses of high carbon steel wires has been assessed. It was found that the application of the multi-roller straightening...

متن کامل

developing very fine nanopearlitic structure in a high carbon steel wire before drawing

the effects of steel wire patenting process parameters on very fine interlamellar spacing in the pearlitic steel wire were investigated and the optimized condition of the process was achieved. in this work, the initial nanopearlitic structure was obtained in a 0.72 wt% carbon steel wire before the wire drawing process. the results were the minimum interlamellar spacing of 35 nm and maximum ulti...

متن کامل

static strain aging behavior of low carbon steel drawn wire

the static strain aging is a phenomenon that can change the mechanical properties of low carbon steels. thus, the static strain aging behavior of low carbon steel wires after drawing process is studied. to do so, the wires are austenitized at different temperatures and cooled in different rates. then the wires are drawn and aged at a specific temperature and time. before and after aging of each...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Tetsu-to-Hagane

سال: 1976

ISSN: 0021-1575,1883-2954

DOI: 10.2355/tetsutohagane1955.62.10_1379