On-line analyzer for Ni-Zn alloy electroplated coating on steel.
نویسندگان
چکیده
منابع مشابه
Ni-B Coating Production on Magnesium Alloy by Electroless Deposition
The use of magnesium alloys is limited due to their susceptibility to corrosion although they have many attractive physical and mechanical properties. To increase mechanical and corrosion properties of these alloys, many deposition method and coating types are used. Electroless Ni–B coatings have received considerable interest recently due to its unique properties such as cost-effectiveness, th...
متن کاملQuantitative Analysis of Electroplated Nickel Coating on Hard Metal
Electroplated nickel coating on cemented carbide is a potential pretreatment technique for providing an interlayer prior to diamond deposition on the hard metal substrate. The electroplated nickel coating is expected to be of high quality, for example, indicated by having adequate thickness and uniformity. Electroplating parameters should be set accordingly for this purpose. In this study, the ...
متن کاملCorrosion Protection of Steel Using Nonanomalous Ni-Zn-P Coatings
A novel technique for obtaining nonanomalous Ni-Zn-P coatings with high Ni content ~74 wt % as compared to 15-20 wt % in the conventional plating method! has been developed. These coatings show promise as a replacement for Cd in sacrificially protecting steel. Ni-Zn-P coatings were deposited using an electroless method from a solution containing NiSO4 , complexing agent and ammonium chloride. V...
متن کاملEffect of heat treatment on structure and properties of multilayer Zn-Ni alloy coatings
Composition modulated multilayer alloy (CMMA) coatings of Zn-Ni were electrodeposited galvanostatically on mild steel (MS) for enhanced corrosion protection using single bath technique. Successive layers of Zn-Ni alloys, having alternately different composition were obtained in nanometer scale by making the cathode current to cycle between two values, called cyclic cathode current densities (CC...
متن کاملApplication of Co-Ni-P coating on grain-oriented electrical steel
An electroless plating of Co-Ni-P was applied to a grain-oriented electrical steel substrate resulting in a power loss improvement of approximately 9-11 %. The mean thickness of the coating was found to be 2.15±0.15 μm from Environmental Scanning Electron Microscope (ESEM) images. Shifts of the magnetostriction stress sensitivity curves showed that stress was acting on the substrate corroborate...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: ISIJ International
سال: 1989
ISSN: 0915-1559
DOI: 10.2355/isijinternational.29.894