On ion-permeable membranes formed by anodization of aluminum.
نویسندگان
چکیده
منابع مشابه
Self-ordered anodic aluminum oxide formed by H2SO4 hard anodization.
The self-ordering of nanoporous anodic aluminum oxide (AAO) in the course of the hard anodization (HA) of aluminum in sulfuric acid (H2SO4) solutions at anodization voltages ranging from 27 to 80 V was investigated. Direct H2SO4-HA yielded AAOs with hexagonal pore arrays having interpore distances D(int) ranging from 72 to 145 nm. However, the AAOs were mechanically unstable and cracks formed a...
متن کاملSelective ion-permeable membranes by insertion of biopores into polymersomes.
In nature there are various specific reactions for which highly selective detection or support is required to preserve their bio-specificity or/and functionality. In this respect, mimics of cell membranes and bio-compartments are essential for developing tailored applications in therapeutic diagnostics. Being inspired by nature, we present here biomimetic nanocompartments with ion-selective mem...
متن کامل1. Aluminum anodization
The history of electrochemical oxidation of aluminum dates back to the beginning of the last century. Anodic treatment of aluminum were intensively investigated to obtain protective and decorative films on its surface [1]. More recently, applications of porous alumina with a huge surface area and a relatively narrow pore size distribution have been exploited [2]. For example, several attempts t...
متن کاملOrdered Nanoporous Alumina Membranes Formed in Oxalic/Phosphoric Acid Using Hard Anodization
Highly self-ordered alumina nanopore arrays were fabricated using hard anodization technique in different mixtures of oxalic/phosphoric acid. The phosphoric acid concentration was varied from 0.05 to 0.3 M while the oxalic acid concentration was changed between 0.3 and 0.4 M. The self ordered nanoporous arrays were obtained in anodization voltage changing from 130 to 200 V. The interpore distan...
متن کاملIdeally ordered 10 nm channel arrays grown by anodization of focused-ion-beam patterned aluminum
Arrays of ideally ordered alumina nanochannels with unprecedented ,10 nm pore size, 40–50 nm interpore spacing, and improved channel uniformity have been fabricated by anodizing an aluminum substrate with a guiding pattern on its surface. The pattern is an array of hexagonally close-packed concaves fabricated by focused ion beam direct sputtering; and its lattice constant is carefully matched t...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Surface Finishing Society of Japan
سال: 1989
ISSN: 0915-1869,1884-3409
DOI: 10.4139/sfj.40.685