Failure Investigation of Hydrogen Blistering on Low-strength Carbon Steel
The current study assesses the root causes of hydrogen blisters on low strength carbon steel equipment. For this purpose, some experiments including hardness test, non-destructive test (NDT), metallography, and fractograpghy are conducted. The microstructure of two blisters is assessed by means of optical microscopy and scanning electron microscopy (SEM). The microstructural studies show that t...
متن کاملThe Effect of Hydrogen Content and Welding Conditions on the Hydrogen Induced Cracking of the API X70 Steel Weld
In this study, first,diffusible hydrogen of cellulosic electrode E8010-P1 and low hydrogen electrode E8018-G was measured by mercury displacement method according to ISO3690. Then,the effect of preheating and post-heating on the sensitivity to hydrogen inducedcold cracking in welding of 18mm API5L X70 steel with these electrodes was investigated according to ISO17642-2. The results of visual in...
متن کاملOn the Brittleness of Bayesian Inference
With the advent of high-performance computing, Bayesian methods are becoming increasingly popular tools for the quantification of uncertainty throughout science and industry. Since these methods can impact the making of sometimes critical decisions in increasingly complicated contexts, the sensitivity of their posterior conclusions with respect to the underlying models and prior beliefs is a pr...
متن کاملThe Effect of Hydrogen Content and Welding Conditions on the Hydrogen Induced Cracking of the API X70 Steel Weld
In this study, first,diffusible hydrogen of cellulosic electrode E8010-P1 and low hydrogen electrode E8018-G was measured by mercury displacement method according to ISO3690. Then,the effect of preheating and post-heating on the sensitivity to hydrogen inducedcold cracking in welding of 18mm API5L X70 steel with these electrodes was investigated according to ISO17642-2. The results of visual in...
متن کاملThe effect of absorbed hydrogen on the dissolution of steel
Atomic hydrogen (H) was introduced into steel (AISI 1018 mild steel) by controlled cathodic pre-charging. The resultant steel sample, comprising about 1 ppmw diffusible H, and a reference uncharged sample, were studied using atomic emission spectroelectrochemistry (AESEC). AESEC involved potentiodynamic polarisation in a flowing non-passivating electrolyte (0.6 M NaCl, pH 1.95) with real time r...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Welding Society
سال: 1955
ISSN: 0021-4787,1883-7204
DOI: 10.2207/qjjws1943.24.8-9_324