ON DECARBURIZATION OF STEEL BY DRY AND WET HYDROGEN
نویسندگان
چکیده
منابع مشابه
Measurement of Decarburization of Heat Treated Steel Surfaces
Decarburization is a significant problem in the heat treatment of steels as decarburization is detrimental to wear life and fatigue life of components. This presentation concentrates on its measurement by four procedures. Test results from an interlaboratory test of steels with spheroidize annealed, lamellar pearlite (normalized) and quenched and tempered martensitic microstructures were evalua...
متن کاملEvolution of Akaganeite in Rust Layers Formed on Steel Submitted to Wet/Dry Cyclic Tests
The evolution of akaganeite in rust layers strongly impacts the atmospheric corrosion behavior of steel during long-term exposure; however, the factors affecting the evolution of akaganeite and its mechanism of formation are vague. In this work, wet-dry cyclic corrosion tests were conducted to simulate long-term exposure. Quantitative X-ray diffraction analysis was employed to analyze variation...
متن کاملSliding friction on wet and dry sand.
We show experimentally that the sliding friction on sand is greatly reduced by the addition of some-but not too much-water. The formation of capillary water bridges increases the shear modulus of the sand, which facilitates the sliding. Too much water, on the other hand, makes the capillary bridges coalesce, resulting in a decrease of the modulus; in this case, we observe that the friction coef...
متن کاملSliding Friction on Wet and Dry Sand
Disclaimer/Complaints regulations If you believe that digital publication of certain material infringes any of your rights or (privacy) interests, please let the Library know, stating your reasons. In case of a legitimate complaint, the Library will make the material inaccessible and/or remove it from the website. Please Ask the Library: http://uba.uva.nl/en/contact, or a letter to: Library of ...
متن کاملEffect of surface roughness on steel-steel dry friction coefficient
The influence of surface roughness magnitude and direction on dry static friction coefficient between two similar steel samples has been studied through an experiment. A testing apparatus has been designed and fabricated to measure the friction coefficient for a few forms of surface asperity. According to the results of the experiments, dry friction coefficient is affected by both magnitude and...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 1941
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane1915.27.4_260