On critical hydrogen concentration for hydrogen embrittlement of Fe3Al
نویسندگان
چکیده
منابع مشابه
Prevention of Hydrogen Embrittlement in Steels
The essential facts about the nature of the hydrogen embrittlement of steels have now been known for 140 years. It is diffusible hydrogen that is harmful to the toughness of iron. It follows, therefore, that the harmful influence of diffusible hydrogen can be mitigated by preventing its entry into steel or by rendering it immobile once it penetrates the material. This review deals with the meth...
متن کاملStudy on Temper Embrittlement and Hydrogen Embrittlement of a Hydrogenation Reactor by Small Punch Test
The study on temper embrittlement and hydrogen embrittlement of a test block from a 3Cr1Mo1/4V hydrogenation reactor after ten years of service was carried out by small punch test (SPT) at different temperatures. The SPT fracture energy Esp (derived from integrating the load-displacement curve) divided by the maximum load (Fm) of SPT was used to fit the Esp/Fm versus-temperature curve to determ...
متن کاملPitting-induced hydrogen embrittlement of magnesium- aluminium alloy
In this study, the pitting corrosion susceptibility and its role on the hydrogen embrittlement behavior of AZ80 magnesium alloy were studied using slow strain rate testing (SSRT), electrochemical technique and immersion test method. The electrochemical and immersion tests in chloride-containing solution revealed severe pitting corrosion in the alloy. The SSRT results of the alloy under continuo...
متن کاملHydrogen Embrittlement Behavior of a 1700 MPa-Class Ultrahigh Strength Steel Containing Hydrogen Traps
Eiji Akiyama , Songjie Li , Yuuji Kimura , Kaneaki Tsuzaki , Nobuyoshi Uno c a National Institute for Materials Science 1-2-1 Sengen, Tsukuba, Ibaraki 305-0047, Japan b School of Materials Science and Engineering, University of Science and Technology Beijing, No. 30 Xueyuan Road, Hidian Zone, Beijing 100083, China c Nippon Steel and Sumikin Metal Products Co, Ltd, SA Bldg., 17-12 Kiba 2-chome, ...
متن کاملHydrogen embrittlement of aluminum: the crucial role of vacancies.
We report first-principles calculations which demonstrate that vacancies can combine with hydrogen impurities in bulk aluminum and play a crucial role in the embrittlement of this prototypical ductile solid. Our studies of hydrogen-induced vacancy superabundant formation and vacancy clusterization in aluminum lead to the conclusion that a large number of H atoms (up to 12) can be trapped at a s...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Bulletin of Materials Science
سال: 2001
ISSN: 0250-4707,0973-7669
DOI: 10.1007/bf02706731