Octahedral Cu2O-modified TiO2 nanotube arrays for efficient photocatalytic reduction of CO2
نویسندگان
چکیده
منابع مشابه
Photocatalytic reduction of methylene blue by TiO2 nanotube arrays: effects of TiO2 crystalline phase
TiO2 nanotube arrays were synthesized by anodization of Ti metal sheets followed by thermal annealing at elevated temperatures from 400 to 600 C. Scanning electron microscopic measurements showed that dense arrays of nanotubes were produced with the inner diameter about 100 nm, wall thickness 35 nm, and length about 10 lm. X-ray diffraction measurements showed that the as-prepared nanotubes wer...
متن کاملSelf-Organized TiO2–MnO2 Nanotube Arrays for Efficient Photocatalytic Degradation of Toluene
Vertically oriented, self-organized TiO2–MnO2 nanotube arrays were successfully obtained by one-step anodic oxidation of Ti–Mn alloys in an ethylene glycol-based electrolyte. The as-prepared samples were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), UV-Vis absorption, photoluminescence spectroscopy, X-ray diffraction (XRD), and micro-Raman spec...
متن کاملStructural manipulation of the photocatalytic activity of TiO2 nanotube arrays
Highly ordered TiO2 nanotube arrays on Ti substrates were prepared by an electrochemical anodization process in a mixture of glycerol and water containing 0.5 wt% NH4F and then thermally annealed from 400 C to 600 C. The sample structures were characterized by scanning electron microscopy and X-ray diffraction measurements, where the nanotube pore diameter and length were found to increase with...
متن کاملPhotocatalytic methane decomposition over vertically aligned transparent TiO2 nanotube arrays.
We report here on a study of vertically aligned TiO(2) nanotube arrays grown by the one-step anodic oxidation technique and their photocatalytic performance for methane decomposition. Quantitative activity data as a function of film thickness is obtained.
متن کاملPhotocatalytic performance of Cu2O-loaded TiO2/rGO nanoheterojunctions obtained by UV reduction
A novel dot-like Cu2O-loaded TiO2/reduced graphene oxide (rGO) nanoheterojunction was synthesized via UV light reduction for the first time. Cu2O with size of ca. 5 nm was deposited on rGO sheet and TiO2 nanosheets. The products were characterized by infrared spectroscopy, Raman spectrum, UV-Vis diffuse reflectance spectra, XPS techniques, photoluminescence spectra. The results demonstrated tha...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Chinese Journal of Catalysis
سال: 2015
ISSN: 1872-2067
DOI: 10.1016/s1872-2067(15)60991-3