Obtaining Alumina from Kaolin Clay via Aluminum Chloride
نویسندگان
چکیده
منابع مشابه
Preparation of Γ-alumina from Aluminum Aminoalkoxides
The synthesis of materials with tailored properties is one of the most active areas of material science [1, 2]. Among so many materials, γ-alumina due to the significant application in catalysis, electronic and ceramic industry has been studied extensively [3]. Various processes have been employed for the preparation of high quality alumina, including sol-gel processing from aluminum alkoxides....
متن کاملPhase Transformations of α-Alumina Made from Waste Aluminum via a Precipitation Technique
We report on a recycling project in which α-Al(2)O(3) was produced from aluminum cans because no such work has been reported in literature. Heated aluminum cans were mixed with 8.0 M of H(2)SO(4) solution to form an Al(2)(SO(4))(3) solution. The Al(2)(SO(4))(3) salt was contained in a white semi-liquid solution with excess H(2)SO(4); some unreacted aluminum pieces were also present. The solutio...
متن کاملOptimizing of Iron Bioleaching from a Contaminated Kaolin Clay by the Use of Artificial Neural Network
In this research, the amount of Iron removal by bioleaching of a kaolin sample with high iron impurity with Aspergillus niger was optimized. In order to study the effect of initial pH, sucrose and spore concentration on iron, oxalic acid and citric acid concentration, more than twenty experiments were performed. The resulted data were utilized to train, validate and test the two layer artificia...
متن کاملProduction of γ-Al2O3 from Kaolin
The paper reports a process for synthesis of γ-alumina from kaolin. Kaolin was transformed to meta-kaolin by calcination at 800 ̊C for 2h. γ-alumina powder was synthesized through extracting alumina from metakaolin via H2SO4 and meta-kaolin reactions and consequently precipitation in ethanol, which led to form the aluminum sulfate. The precipitated aluminum sulfate was dried and calcined at 900 ̊...
متن کاملOn the Study of Mechanical Properties of Aluminum/Nano-Alumina Composites Produced via Powder Injection Molding
Powder Injection Molding (PIM) is a precision manufacturing process used for production of advanced composites. Mixing of polymeric binder with metal powders, molding of feedstock, de-binding of brown parts and sintering of green samples are four main steps of this process. In the present study, the compounds containing multi-component binder system and aluminum/ nano-alumina (0-9 wt.%) powders...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials
سال: 2019
ISSN: 1996-1944
DOI: 10.3390/ma12233938