Observation of Initial Stage of Co and Co-Ni Alloy Film Formation by Pulsed Current Electrodeposition.
نویسندگان
چکیده
منابع مشابه
Preparation of Ni-Co Alloy Foils by Electrodeposition
Electrodeposition of Ni-Co alloy foils on titanium substrate was performed in an acid chloride-sulphate bath. The influences of electrodeposition parameters such as current density, temperature, pH value, cobalt sulphate and saccharin concentration on composition and current efficiency were investigated in detail. The morphology and the microstructure of deposits were analyzed by SEM and XRD, r...
متن کاملTernary Ni-Fe-Co Alloys Nanowire Electrodeposition
Nanowire is a cylindrical nano-structure with nanometer dimensions. In this research, the studied nanowire was made from the magnetic triple Ni-Fe-Co alloy.
 We utilized ordered porous anodic aluminum oxide as a template for the nanowire deposition. The nanowire arrays were electrodeposited in the cylindrical pores of the oxide layer by AC potential in a simple sulfate bath. Then the relatio...
متن کاملTernary Ni-Fe-Co Alloys Nanowire Electrodeposition
Nanowire is a cylindrical nano-structure with nanometer dimensions. In this research, the studied nanowire was made from the magnetic triple Ni-Fe-Co alloy. We utilized ordered porous anodic aluminum oxide as a template for the nanowire deposition. The nanowire arrays were electrodeposited in the cylindrical pores of the oxide layer by AC potential in a simple sulfate bath. Then the relation ...
متن کاملEffect of pulsed current densities on co-electrodeposition of Graphene Oxide/ Calcium-Phosphate coatings and their biocompatibility
In this study, calcium-phosphate (Ca-P) and graphene oxide (GO)/ calcium-phosphate (Ca-P) coatings were electrodeposited with different pulsed current densities on TiO2 nanotubes. Results showed that the co-electrodeposition rate in the presence of GO, especially at low current densities of 2 and 5 mA/cm2, significantly decreased. This might be due to the large size of GO sheets as compared to ...
متن کاملMagnetic Properties and Structural Study of Ni-Co/Cu Multilayers Prepared by Electrodeposition Method
Ni-Co/Cu multilayers have been grown by electrodeposition method from a single electrolyte (based on Ni(SO4).6H2O, Co(SO4).7H2O, Cu(SO4) and H3BO3) using galvanostatic control on titanium sublayers. The X-ray diffraction (XRD) patterns confirmed the multilayered structure with the nanometer thicknesses. Also, electron diffraction x-ray (EDX) analysis confirmed the purity of deposited samples. ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Hyomen Kagaku
سال: 2000
ISSN: 0388-5321,1881-4743
DOI: 10.1380/jsssj.21.488