Novel sol-gel SiO2-NaGdF4 transparent nano-glass-ceramics
نویسندگان
چکیده
منابع مشابه
Upconversion properties of a transparent Er3þ–Yb3þ co-doped LaF3–SiO2 glass-ceramics prepared by sol–gel method
Transparent 0.1ErF3–0.1YbF3–5LaF3–94.8SiO2 (mol%) glass-ceramics was prepared by sol–gel method. Efficient upconversion emissions at 379, 407, 450, 490, 520, 540 and 660 nm were observed under 973 nm excitation. The signal at 379 nm is only 4.5 times weaker than the signal at 520 nm, that is readily visible by the naked eyes even with a pump power of 27 mW, indicating that this sample is a very...
متن کاملTransparent Glass-Ceramics Produced by Sol-Gel: A Suitable Alternative for Photonic Materials
Transparent glass-ceramics have shown interesting optical properties for several photonic applications. In particular, compositions based on oxide glass matrices with fluoride crystals embedded inside, known as oxyfluoride glass-ceramics, have gained increasing interest in the last few decades. Melt-quenching is still the most used method to prepare these materials but sol-gel has been indicate...
متن کاملTm3+ Modified Optical Temperature Behavior of Transparent Er3+-Doped Hexagonal NaGdF4 Glass Ceramics
Er3+-doped and Er3+-Tm3+-co-doped transparent hexagonal NaGdF4 glass ceramics are fabricated via melt-quenching method. The emissions of Er3+-doped NaGdF4 glass ceramics are adjusted from the green to red by varying the concentration of Tm3+ ion under the excitation of 980 nm. The spectrum, thermal quenching ratio, fluorescence intensity ratios, and optical temperature sensitivity of the transp...
متن کاملMicrostructure of Transparent Strontium Fresnoite Glass-Ceramics
Glass-ceramics grown from a glass of the composition Sr2TiSi2.45O8.9 (STS 45) are analyzed by scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD). Oriented nucleation with the c-axes preferably perpendicular to the surface is detected. A very strong 001-texture is observed after only 10 μm of growth into the bulk, making this the first system in which an orientation p...
متن کاملFe-Doped Sol-Gel Glasses and Glass-Ceramics for Magnetic Hyperthermia
This work deals with the synthesis and characterization of novel Fe-containing sol-gel materials obtained by modifying the composition of a binary SiO₂-CaO parent glass with the addition of Fe₂O₃. The effect of different processing conditions (calcination in air vs. argon flowing) on the formation of magnetic crystalline phases was investigated. The produced materials were analyzed from thermal...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Non-Crystalline Solids
سال: 2019
ISSN: 0022-3093
DOI: 10.1016/j.jnoncrysol.2019.05.023