Non-isothermal degradation kinetics of filled with rise husk ash polypropene composites
نویسندگان
چکیده
منابع مشابه
Non-isothermal degradation kinetics of filled with rise husk ash polypropene composites
The thermal stability and kinetics of non-isothermal degradation of polypropene and polypropene composites filled with 20 mass% vigorously grounded and mixed raw rice husks (RRH), black rice husks ash (BRHA), white rice husks ash (WRHA) and Aerosil Degussa (AR) were studied. The calculation procedures of Coats – Redfern, Madhysudanan et al., Tang et al., Wanjun et al. and 27 model kinetic equat...
متن کاملNon-Isothermal Degradation Kinetics of High Energy Protons Irradiated Polyvinyl Butyral
This research is aimed to undertake a comparative study on stability and thermal degradation kinetics of un-irradiated and high energy protons irradiated polyvinyl butyral (PVB) based on weight loss analysis and non-isothermal approaches. The weight loss by the un-irradiated PVB upon heating was found to be in two stages but due to high energy protons accelerated exposure following by chemical ...
متن کاملNon-isothermal kinetics of thermal degradation of chitosan
BACKGROUND Chitosan is the second most abundant nitrogen containing biopolymer in nature, obtained from the shells of crustaceans, particularly crabs, shrimp and lobsters, which are waste products of seafood processing industries. It has great potential application in the areas of biotechnology, biomedicine, food industries, and cosmetics. Chitosan is also capable of adsorbing a number of metal...
متن کاملNon–isothermal kinetics of degradation of chitin and chitosan
Thermogravimetric studies of chitin and chitosan in air atmosphere were carried out at six rates of linear increase of the temperature. The kinetics and mechanism of the thermal decomposition reaction were evaluated from the TG data using recommended from ICTAC kinetics committee isoconversional calculation procedure of Kissinger-Akahira-Sunose, as well as 27 mechanism functions. The values of ...
متن کاملNon-Isothermal Dehydration Kinetics of Diphasic Mullite Precursor Gel
Aluminosilicate gel precursor having mullite composition was synthesized from inorganic salts of aluminum and silicon by employing the sol-gel method. Chemical analysis, surface area and bulk density measurements were performed to characterize the dried gel. The course of the mullitization was examined by FT-IR analysis which confirmed the diphasic nature of the gel. ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Express Polymer Letters
سال: 2008
ISSN: 1788-618X
DOI: 10.3144/expresspolymlett.2008.18